Effects of La/Ho co-substitution on structure and multiferroic characteristics of BiFeO₃ ceramics

Qing Tian Li,Lu Liu,Xiao Li Zhu,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1063/5.0174827

IF: 2.877

2023-01-01

Journal of Applied Physics

Abstract:The effects of La/Ho co-substitution on multiferroic characteristics were investigated for BiFeO3 ceramics together with structure evolution. The symmetry in Bi1-x(La0.65Ho0.35)(x)FeO3 ceramics changed from R3c to Pna2(1) and finally Pbnm with increasing x. Ferroelectricity was significantly improved with La/Ho co-substitution, and P-r reached the maximum of 30.9 mu C/cm(2) at 160 kV/cm at x = 0.16, where the R3c/Pna2(1) morphotropic phase boundary was determined. The weak ferromagnetism was released as the symmetry changed from R3c to Pna2(1), and subsequently the saturated M-H loop could be determined gradually with increasing x, and M-r increased continuously. The electric field-controlled magnetism could be characterized by the significant magnetism variation due to the electric field-induced transition of Pna2(1)/R3c, which occurred during the poling process, and this transition became reversible by the help of annealing after poling. Compared with the situation of Bi1-xNdxFeO3 (the ion radius is the same as the effective one of La0.65Ho0.35), the present co-substituted BiFeO3 ceramics exhibited superior electric field-induced transition of Pna2(1)/R3c with a maximum change rate of 47.03% in remanent magnetization under an electric field, which enhanced the magnetoelectric effect.