Interfacial characteristics of Na2FePO4F and its carbon coated material for lithium/sodium hybrid ion battery

Mingjun Lu,Rongting Guo,Wei Li,Yiju Lv,Fushun Tang,Weiyi Feng,Zheng Liu,Guo-Cheng Han,Zhihua Zhan
DOI: https://doi.org/10.1016/j.jelechem.2022.116772
IF: 4.598
2022-10-01
Journal of Electroanalytical Chemistry
Abstract:The interfacial characterization of the cathode material Na2FePO4F with carbon capping material Na2FePO4F@C taking bagasse as the carbon source is reported. Both the higher-capacity Na2FePO4F@C material (93 mAh/g) and lower-capacity Na2FePO4F material (10 mAh/g) showed different degrees of capacity decay during cycling. The rupture and spontaneous repair process of the solid electrolyte interface (SEI) film resulting in increased impedance and blocked charge transfer, as well as irreversible changes in the surface microstructure of the electrode material after cycling, which are responsible for the decrease in capacity. The XRD and FTIR results before and after cycling shown that the characteristic peaks of the carbon coated material Na2FePO4F@C and raw material Na2FePO4F were consistent, indicated that their functional groups and crystalline structures are not the main causes of capacity decay at low cycling times (within 50 cycles).
chemistry, analytical,electrochemistry
What problem does this paper attempt to address?