A new lithium-ion batteries derivated from waste bagasse: Preparation, characterization and application

Huiting Ai,Wei Li,Zheng Liu,Dan Sun,Hanzi Zhou,Guo-Cheng Han
DOI: https://doi.org/10.1016/j.jallcom.2020.157156
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>A cathode material carbon-coated Na<sub>2</sub>FePO<sub>4</sub>F (Na<sub>2</sub>FePO<sub>4</sub>) was reported which were derivated from waste biomass bagasse as carbon source were prepared by wet ball milling and in-situ pyrolysis, due to the low cost and easy availability of biomass carbon materials. The performance results shown that the Na<sub>2</sub>FePO<sub>4</sub> composite material prepared under the condition of 10% carbon source and calcination temperature of 650 °C crystallized well, and the carbon material was coated on the external of Na<sub>2</sub>FePO<sub>4</sub>F well with no damaging the crystal structure of the material. The first ring discharging specific capacity with Na<sub>2</sub>FePO<sub>4</sub> was 128 mA h g<sup>−1</sup> based on 0.1 C current density, which was a three-fold increase compared with the carbon-free coated material Na<sub>2</sub>FePO<sub>4</sub>F (40 mA h g<sup>−1</sup>). The coulomb efficiency of Na<sub>2</sub>FePO<sub>4</sub> cathode material remained above 97.8% after 30 cycles at 0.1 C. This work applied biomass carbon materials to hybrid ion batteries, offering more possibilities for the development of sodium-based fluorophosphate materials for lithium-ion batteries coated with low-cost biomass-based carbon materials.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?