Abstract:Huge amount of flue gas desulphurization (FGD) gypsum not only occupies the farmland but also causes severe pollution to the surrounding environment. The most effective way to achieve a high-value utilization of FGD gypsum is to prepare short columnar α-calcium sulfate hemihydrate (α-HH) since short columnar crystals show better mechanical strength than needle-like ones. Here, malic acid, a prolific, inexpensive and environment-friendly modifier was explored for the first time to effectively tune the crystal morphology of α-HH prepared from FGD gypsum in glycerol-water-NaCl solutions. When the concentration of malic acid reached 18.54 × 10-4 mol/kg, α-HH crystals with an average aspect (length-to-diameter) ratio of 1.9 (compared to 29.4 in the absence of malic acid) were prepared. The selective complexation of malic acid with Ca active sites on different α-HH crystal planes played a dominant role in the α-HH crystal morphology transformation, which was then explained by the surface broken bonds theory for the first time. The broken bond number per active Ca atom (Nbper Ca) and broken bond density of Ca atoms (DbCa) on the (2 0 4) end plane were larger than those on the (0 2 0) or (2 0 0) side planes. Therefore, the (2 0 4) end plane was more reactive with organics, resulting in the preferential adsorption of malic acid on the end planes, which reduced the specific surface energy of (2 0 4) and led to an increased exposure of this plane and a decreased exposure of (0 2 0) or (2 0 0) side planes in the final α-HH crystals. Consequently, using malic acid as modifier, the α-HH crystal gradually transformed from a needle-like shape to a short columnar one. This work provided important insights into and perspectives for the selection of crystal modifiers and explanation of the mechanism during the preparation of calcium-containing crystals with controllable morphology.

Effect of sodium fluoride on the crystal regulation of high-strength α-hemihydrate gypsum from calcium sulphate dihydrate and phosphogypsum

Effect Of Potassium Sodium Tartrate And Sodium Citrate On The Preparation Of Alpha-Calcium Sulfate Hemihydrate From Flue Gas Desulfurization Gypsum In A Concentrated Electrolyte Solution

Influence of crystal modifier on the preparation of α-hemihydrate gypsum from phosphogypsum

Influence of crystal-transforming agent on the performance and mechanism of α-high-strength gypsum prepared from FGD gypsum

Effect of Fluorine and Phosphorus Impurities in Phosphogypsum on Microstructure and Mechanism of α‐Type Hemihydrate Gypsum Crystals

Effect of soluble fluorine on the hydration, strength and microstructure of hemihydrate phosphogypsum

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Effect of modifiers on crystalizing habit and mechanical strength of α-hemihydrate gypsum prepared from PG by an autoclaved method

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Effects of glutaric acid, tricarballylic acid and citric acid on the morphology of α-hemihydrate gypsum: Experimental and DFT simulation studies

Influence of Seed Crystal and Modifier on the Morphology of α-calcium Sulfate Hemihydrate Prepared by Salt Solution Method in Pilot Scale

Effect of Ph on the Preparation of Alpha-Calcium Sulfate Hemihydrate from Fgd Gypsum with the Hydrothermal Method

Retarding effect of impurities on the transformation kinetics of FGD gypsum to α-calcium sulfate hemihydrate under atmospheric and hydrothermal conditions

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Study on activation of fluorogypsum by sodium sulfate and sodium nitrite

Preparation of α-CaSO4·½H2O with tunable morphology from flue gas desulphurization gypsum using malic acid as modifier: A theoretical and experimental study

Preparing sulfoaluminate cement using phosphogypsum as the only calcium oxide source: Effects of fluoride impurities

Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum