Abstract:This study investigates the effectiveness of polyether block amide (PEBA) thermoplastic elastomeric nanofibers in reducing low-velocity impact damage across three carbon fiber composite lay-up configurations: a cross-ply [0°/90°]2s (CP) and a quasi-isotropic [0°/45°/90°/−45°]s (QI) lay-up utilizing unidirectional plies, and a stacked woven [(0°,90°)]4s (W) lay-up using twill woven fabric plies. The flexural strength and interlaminar shear strength of the composites remained unaffected by the addition of nanofibers: around 750 MPa and 63 MPa for CP, 550 MPa and 58 MPa for QI, and 650 MPa and 50 MPa for W, respectively. The incorporation of nanofibers in the interlaminar regions resulted in a substantial reduction in projected damage area, ranging from 30% to 50% reduction over an impact energy range of 5–20 J. Microscopic analysis showed that especially the delamination damage decreased in toughened composites, while intralaminar damage remained similar for the cross-ply and quasi-isotropic lay-ups and decreased only in the woven lay-up. This agrees with the broad body of research that shows that interleaved nanofibers result in a higher delamination resistance due to toughening mechanisms related to nanofiber bridging of cracks. Despite their ability to mitigate delamination during impact, nanofibers showed limited positive effects on Compression After Impact (CAI) strength in quasi-isotropic and cross-ply composites. Interestingly, only the woven fabric composites demonstrated improved CAI strength, with a 12% improvement on average over the impact energy range, attributed to a reduction in both interlaminar and intralaminar damage. This study indicates the critical role of fiber integrity over delamination size in determining CAI performance, suggesting that the delaminations are not sufficiently large to induce buckling of sub-layers, thereby minimizing the effect of nanofiber toughening on the CAI strength.

Enhancing resistance to low-velocity impact of electrospun-manufactured interlayer-strengthened CFRP by using infrared thermography

Enhancing CFRP Laminates with Plasma Jet Arrays: A Study of Interlaminar Mechanical Properties

Extreme temperature influence on low velocity impact damage and residual flexural properties of CFRP

Impact responses and residual flexural properties of narrow CFRP laminates

Reconstruction of Impact Damage in CFRP Laminate Based on Infrared Thermography

Low-Velocity Impact Behavior and Damage Characteristics of CFRP Laminates

Interfacial Strengthening and Self-Monitoring in Carbon Fiber-Reinforced Composites via Carbon Nanotube-Based Damage Sensors

Electrospun nanofiber interleaving through double infusion method to induce pseudo‐ductile damage resistance response in carbon/epoxy composites

Low-Velocity Impact Resistance and Compression After Impact Strength of Thermoplastic Nanofiber Toughened Carbon/Epoxy Composites with Different Layups

A novel force-temperature model for evaluating internal forces in CFRP by means of infrared thermography

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Electrospun short nanofibers to improve damage resistance of carbon fiber composites

Experimental and theoretical study on residual ultimate strength after impact of CF/PEEK-titanium hybrid laminates with nano-interfacial enhancement

Study on anisotropic heat transfer and thermal damage in nanosecond pulsed laser processing of CFRP

Interlaminar toughening in structural carbon fiber/epoxy composites interleaved with carbon nanotube veils

Improving interlaminar fracture toughness and compression after impact strength of carbon fiber reinforced epoxy composites by interleaving electrospinning polyethersulfone nanofiber

Enhanced interlaminar fracture toughness of CF/PEEK laminates by interleaving CNT-decorated PEEK films

Low-velocity impact and compression-after-impact behaviors of twill woven carbon fiber/glass fiber hybrid composite laminates with flame retardant epoxy resin

Damage tolerancing in carbon fiber-reinforced polymer (CFRP) laminates under combined impact fatigue and environmental conditioning

Experimental investigation on damage mechanism of GFRP laminates embedded with/without steel wire mesh under low-velocity-impact and post-impact tensile loading

Effect of laser shock peening without protective coating on surface integrity of titanium-based carbon-fibre/epoxy laminates