Three-Dimensional Printing of Lignocellulose Structures: Improving Mechanical Properties and Shape Fidelity

Yangxiaozhe Jiang,Muhammad Latif,Jaehwan Kim
DOI: https://doi.org/10.1021/acsomega.3c10101
IF: 4.1
2024-06-11
ACS Omega
Abstract:Additive manufacturing of nanocellulose (NC) materials is an emergent technological domain that facilitates the fabrication of complex and environment-friendly structures that mitigate greenhouse gas emissions. However, printing high concentrations of NC into intricate structures encounters substantial challenges due to inadequate adhesion between the printed layers attributed to a high cellulose solid content, resulting in low shape fidelity and mechanical properties. Therefore, to address...
chemistry, multidisciplinary
What problem does this paper attempt to address?
The main problems that this paper attempts to solve are to improve the low mechanical properties and poor shape fidelity encountered in the 3D printing process of high - concentration nanocellulose (NC) materials. Specifically: 1. **Low mechanical properties**: After 3D printing, high - concentration nanocellulose materials have low mechanical properties due to insufficient inter - layer adhesion. 2. **Poor shape fidelity**: During the 3D printing process, high - concentration nanocellulose materials are prone to problems such as poor inter - layer adhesion and shrinkage deformation during the drying process, resulting in poor shape fidelity of the final printed structure. To solve these problems, the author proposes a method, that is, adding lignin (abbreviated as LG) to high - concentration nanocellulose slurry to improve the inter - layer adhesion, thereby improving the mechanical properties and shape fidelity of 3D - printed structures. By optimizing the lignin content and the drying conditions after 3D printing, the author has successfully prepared 3D - printed structures with high mechanical strength and good shape fidelity. ### Main research contents: - **Material preparation**: Prepared high - concentration nanocellulose slurries with different lignin contents. - **3D printing**: Used a twin - screw extruder for 3D printing and dried under clean - room conditions. - **Performance testing**: Evaluated the mechanical properties and chemical interactions of 3D - printed structures by means of bending tests, scanning electron microscope (SEM) observation, Fourier transform infrared spectroscopy (FTIR) analysis, etc. ### Key results: - **Mechanical properties**: The optimized 0.5LG - NC structure shows a significant improvement in mechanical properties, with a flexural strength reaching 102.93 ± 0.96 MPa and an elastic modulus of 9.05 ± 0.07 GPa. - **Shape fidelity**: The 3D - printed structure maintains good shape fidelity after drying, with a low volume shrinkage rate and good repeatability. - **Chemical interactions**: FTIR analysis has confirmed the hydrogen - bond interaction between lignin and nanocellulose, which enhances the inter - layer adhesion. ### Application prospects: This research provides new ideas for manufacturing high - performance and environmentally - friendly 3D - printed structures, and has important potential value especially in applications in the engineering and biomedical fields.