Sequential‐dip‐coating processed mixed organic and inorganic perovskite film from halide‐free lead precursor for efficient perovskite solar cells

Zobia Irshad,Muhammad Adnan,Ho‐Joong Kim,Jae Kwan Lee

DOI: https://doi.org/10.1002/bkcs.12882

2024-06-05

Bulletin of the Korean Chemical Society

Abstract:The development of FA1MA1−yPbI3−xBrx perovskite films through an all‐sequential‐dip‐coated (SDC) deposition method marks a significant advancement in the field of perovskite solar cells (PrSCs). This novel approach utilizes an aqueous non‐halide lead precursor, promoting an environmentally friendly and cost‐effective alternative to traditional methods. The strategic modulation of FABr concentration in the precursor solution enables precise control over the bromine content within the perovskite crystal lattice, enhancing surface coverage and crystallinity. Such improvements are crucial for achieving high device performance and stability. The SDC method not only demonstrates increased efficiency due to the use of benign solvents but also shows promise for scaling up to large‐area PrSC devices, overcoming limitations associated with conventional spin‐casting techniques. This innovative synthesis strategy could potentially lead to more sustainable and scalable production of high‐performance PrSCs, contributing to the advancement of solar energy technology. A novel all‐sequential‐dip‐coated (SDC) deposited FA1MA1−yPbI3−xBrx perovskite films have been synthesized from an aqueous non‐halide lead precursor towards an environmentally benign, cost‐effective, and efficient approach for high‐performance perovskite solar cells (PrSCs). The mixed‐cationic FA1MA1−yPbI3−xBrx perovskite layers ensure the fractional incorporation of Br into the perovskite crystal lattice. The insertion of Br contents was regulated by modulating the FABr concentration into the FABr/MAI mixed‐cationic precursor solution. The incorporation of minor FABr into MAI helps to improve the surface coverage and crystallinity of the synthesized per‐ovskite layer in contrast to the other perovskite films prepared with higher FABr content under the same environment. The PrSCs with these FA1MA1−yPbI3−xBrx perovskite layers displayed good de‐vice performances and stability with a PCE of 11.1%. These outcomes reveal that the synthesis of FA1MA1−yPbI3−xBrx perovskite films with the SDC approach is more efficient because of the use of environmentally benign solvents for synthesizing lead and perovskite layers.

chemistry, multidisciplinary