Abstract:Cold-drawn pearlitic steel wires exhibit ultrahigh strength and have important applications where high strength and wear resistance are required. The hypereutectoid compositions present a promising potential for increasing the mechanical properties, especially the strength. The austenitization process strongly influences the following pearlitic microstructure and thus the mechanical properties. Continuous heating is always used in the industrial processing. However, the austenitization of pearlite in hypereutectoid steels during continuous heating has not been investigated systematically. In this work, the dilatometer and DSC were employed to investigate the austenitization kinetics of hypereutectoid steels during continuous heating. Microstructure evolution was observed with SEM and EBSD. The dilatometer and DSC curves were analyzed with derivative method. The whole austenitization can be divided into five stages: initial microstructure, reverse eutectoid transformation, retained cementite dissolution, homogenization and homogeneous austenite. Tangent method was used for measuring the critical temperatures of different stages. Experimental determination of transformed fraction was obtained through the lever method. Calculation with Thermo-Calc and Dictra software was carried out for the austenitization and considered to be a reasonable result by comparing with the experimental data. There is a turning point for the reduction rate of cementite and formation of austenite at the finishing temperature of reverse eutectoid transformation, which is similar with the austenitization in low carbon steel and spheroidal pearlite of hypereutectoid steel. Effects of heating rates, initial microstructure and carbon content were studied by varying the relevant parameters. Higher heating rate in- creases the starting and finishing temperatures of reverse eutectoid transformation and widens the temperature range, has no effect on the finishing temperature of retained cementite dissolution, increases the finishing temperature of homogenization. Coarser initial pearlitic microstructure increases the starting and finishing temperatures, widens the temperature range for reverse eutectoid transformation, increases the finishing temperature for retained cementite dissolution and homogenization. Enhancement of carbon content has little effect on the reverse eutectoid transformation, but increases the finishing temperature for retained cementite dissolution and homogenization. The effects mentioned above on the austenitization kinetics were discussed for mechanism analysis and compared with the observations of relevant systems provided by other research.

Development of significantly hard hypereutectoid plain carbon steel through incomplete austenitization based cyclic quenching treatmentEntwicklung eines signifikant harten übereutektoiden Kohlenstoff‐Glattstahls durch eine zyklische Abschreckung mit unvollständiger Austenitisierung

Microstructural modifications and changes in mechanical properties during cyclic heat treatment of 0.16% carbon steel

Attainment of an exceptionally high strength in low-carbon steel along with modest ductility through a novel heat treatment route

Increasing the Strength and Impact Toughness of Carbon Steel Using a Nanosized Eutectoid Resulting from Time-Controlled Quenching

Microstructural Evolution of a Low-Carbon Steel during Application of Quenching and Partitioning Heat Treatments after Partial Austenitization

Formation of Bainite in a Low‐Carbon Steel at Slow Cooling Rate – Experimental Observations and Thermodynamic Validation

Development of Fully Pearlitic Microstructure in a Hypoeutectoid Steel

Investigation of Austenitization During Continuous Heating Process in Hypereutectoid Steels

Hardening of Cylindrical Bars with Water Impinging Jet Quenching Technique

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel

Carbide precipitation and hydrogen embrittlement susceptibility of a 960 MPa grade ultra-high strength steel

Preparation Methods for Lower Bainite after a Continuous Austempering Treatment of Thin Sheets of the Eutectoid Cold Work Steel 80CrV2 (1.2235)

Development of ultra high strength steel with high ductility by air cooling post single stage quench partitioning

Effects of deep cryogenic treatment on the microstructure evolution, mechanical and thermal fatigue properties of H13 hot work die steel

Insight into the induction hardening behavior of a new 0.40% C microalloyed steel: Effects of initial microstructure and thermal cycles

Strengthening and Toughening Mechanisms in Martensitic Steel

Hardness and toughness investigations of deep cryogenic treated cold work die steel

Development and characterization of lower, upper, and inverse bainite in an experimental 0.8wt.% C steel

Differential Microstructure and Properties of Boron Steel Plates Obtained by Water Impinging Jet Quenching Technique

Microstructure and Properties of a Low Carbon Bainitic Steel Produced by Conventional and Inverted Two-Step Austempering Processes