Over 16% Efficiency of Thick‐Film Organic Photovoltaics with Symmetric and Asymmetric Non‐Fullerene Materials as Alloyed Acceptor

Jinhua Gao,Wei Gao,Xiaoling Ma,Jian Wang,Xuelin Wang,Chunyu Xu,Xiaoli Zhang,Jian Zhang,Chuluo Yang,Alex K.-Y. Jen,Fujun Zhang

DOI: https://doi.org/10.1002/solr.202100365

IF: 9.1726

2021-06-24

Solar RRL

Abstract:<p>High-performance organic photovoltaics (OPVs) with relatively thick active layers are essential for large-scale production. In this work, series of OPVs with different active layer thickness were fabricated by using PM6 as donor, BP4T-4F and BP3T-4F with symmetric and asymmetric structures as acceptors. With active layer thickness increasing from 100 nm to 300 nm, the power conversion efficiency (PCE) of BP3T-4F based binary OPVs are slightly decreased from 15.37% to 14.40%, while the PCE of BP4T-4F based binary OPVs are markedly decreased from 16.89% to 14.99%. Two kinds of binary OPVs exhibit distinct PCE and thickness tolerance feature, which may be recombined into ternary OPVs by employing the compatible BP3T-4F and BP4T-4F as alloyed acceptors. The ternary OPVs exhibit a slightly decreased PCE from 16.91% to 16.03% along with active layer thickness from 100 nm to 300 nm, benefiting from the well-optimized phase separation in ternary active layers. It is worth highlighting that fill factor (FF) of 71.47% is achieved in ternary thick-film OPVs. The PCE of 16.03% and FF of 71.47% should be among the highest values among OPVs with 300 nm thick active layers.</p><p>This article is protected by copyright. All rights reserved.</p>

energy & fuels,materials science, multidisciplinary