Abstract:Benefitting from narrow band gap nonfullerene acceptors, continually increasing power conversion efficiency (PCE) endows organic solar cells (OSCs) with great potential for commercial application. Fabricating high-performance OSCs with potential for large-scale coating and nonhalogenated solvent processing is a necessity. Herein, we have proposed the use of nonhalogenated solvents combined with high-temperature blade coating to prepare a PM6 (poly[(2,6-(4,8-bis(5-(2-ethylhexyl-3-fluoro)thiophen-2-yl)benzo[1,2-b:4,5-b′]dithiophene))-alt-(5,5-(1′,3′-di-2-thienyl-5′,7′-bis(2-ethylhexyl)benzo[1′,2′-c:4′,5′-c′]dithiophene-4,8-dione)]):Y6 (2,2′-((2Z,2′Z)-((12,13-bis(2-ethylhexyl)-3,9-diundecyl-12,13-dihydro-[1,2,5]thiadiazolo[3,4-e]thieno[2″,3′′:4′,5′]thieno[2′,3′:4,5]pyrrolo[3,2-g]thieno[2′,3′:4,5]thieno[3,2-b]indole-2,10-diyl)bis(methanylylidene))bis(5,6-difluoro-3-oxo-2,3-dihydro-1H-indene-2,1-diylidene)))blend active layer. The resultant OSCs deliver a PCE of 15.51% when the PM6:Y6 active layer is blade-coated at 90 °C in nonhalogenated o-xylene (o-XY) host solvent containing 1,2-dimethylnaphthalene (DMN) additive. It is found that high-temperature blade coating and nonhalogenated solvent additive DMN can suppress excessive aggregation of Y6 and enhance the crystallinity of PM6 and Y6 by regulating the dynamic process of active layer formation. Finally, an optimized blend morphology with nanofibrous phase separation and enhanced crystallinity are achieved for the PM6:Y6 active layer prepared with high-temperature blade coating and nonhalogenated o-XY:DMN solvents, which not only shortens the film-drying time but also leads to increased charge generation, transport, and collection efficiency. The 1.00 cm2 OSCs prepared with high-temperature blade coating and nonhalogenated solvents exhibit a high PCE of 13.87%. This approach shows great potential for large-area fabrication of OSCs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c23035?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c23035</a>.Normalized absorption spectra, TEM images, and AFM height and phase images of the films prepared under different processing conditions; illuminated J–V characteristics, dependence of VOC and JSC, Eg, VOC, and Eloss of the OSCs prepared at different processing conditions; J1/2–V characteristics of hole-only and electron-only devices prepared under different processing conditions; summarized solubility parameters (δ) of materials and solvents, interaction parameters (χ), and the calculation formula and boiling points of solvents; detailed photovoltaic parameters for the large-area (1.00 cm2) OSCs prepared under different processing conditions (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c23035/suppl_file/am0c23035_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

High-Efficiency Thickness-Insensitive Organic Solar Cells with an Insulating Polymer

High‐Efficiency Organic Solar Cells with Wide Toleration of Active Layer Thickness

High-efficiency Flexible Organic Solar Cells with a Polymer-Incorporated Pseudo-Planar Heterojunction.

Over 18% Efficiency Ternary Organic Solar Cells with 300 nm Thick Active Layer Enabled by An Oligomeric Acceptor

Thickness Insensitive Organic Solar Cells with High Figure‐of‐Merit‐X Enabled by Simultaneous D/A Interpenetration and Stratification

Optimized Charge Transport Channel Enables Thick-Film All-Small-Molecule Organic Solar Cells

Thickness-Insensitive Anode Interface Layer for High-Efficiency Organic Solar Cells

π‐π Stacking Modulation via Polymer Adsorption for Elongated Exciton Diffusion in High‐Efficiency Thick‐Film Organic Solar Cells

A Pseudo Planar Heterojunction Structure for Eco‐Friendly Printable Organic Solar Cells Achieving 19.05% Efficiency

High‐Performance Green Thick‐Film Ternary Organic Solar Cells Enabled by Crystallinity Regulation

Thick‐Film Organic Solar Cells Achieving over 11% Efficiency and Nearly 70% Fill Factor at Thickness over 400 Nm

Highly Efficient and Thickness-Tolerable Bulk Heterojunction Polymer Solar Cells Based on P3HT Donor and a Low-Bandgap Non-Fullerene Acceptor

Surpassing 13% Efficiency for Polythiophene Organic Solar Cells Processed from Nonhalogenated Solvent

High Performance Thick‐Film Nonfullerene Organic Solar Cells with Efficiency over 10% and Active Layer Thickness of 600 Nm

Vertically Optimized Phase Separation with Improved Exciton Diffusion Enables High-Efficiency Organic Solar Cells with Thick Active Layers

High‐Efficiency Binary Organic Solar Cells Enabled by Pseudo‐Bilayer Configuration in Dilute Solution

Efficient Organic Ternary Solar Cells Employing Narrow Band Gap Diketopyrrolopyrrole Polymers and Nonfullerene Acceptors

π-Extended Nonfullerene Acceptors for Efficient Organic Solar Cells with a High Open-Circuit Voltage of 0.94 V and a Low Energy Loss of 0.49 eV

Additive and High-Temperature Processing Boost the Photovoltaic Performance of Nonfullerene Organic Solar Cells Fabricated with Blade Coating and Nonhalogenated Solvents

Fabrication of High V OC Organic Solar Cells with a Non-Halogenated Solvent and the Effect of Substituted Groups for “Same-A-Strategy” Material Combinations

Overcoming Space‐Charge Effect for Efficient Thick‐Film Non‐Fullerene Organic Solar Cells