Abstract:Phosphogypsum (PG) is a kind of industrial solid waste with high impurity content and low utilization rate. In this study, α-hemihydrate gypsum (α-HH) was synthesized from PG in H3PO4–H2O solution (wet-process phosphoric acid solution and phosphoric acid solution) under atmospheric pressure. The crystal morphology of α-HH was controlled by adding F and Al compound regulators, and the mechanical properties of α-HH were improved. The difference of α-HH synthesized by PG with different qualities was analyzed, and the mechanism of α-HH morphology was studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy-dispersive spectroscopy (EDS). Results showed that in the wet-process phosphoric acid solution, α-HH synthesized from white PG (by H3PO4–H2SO4 two-step method) had better whiteness, purity, and mechanical properties compared with that from industrial PG, and the performance indexes of the α-HH products met the requirements of α50 grade in JC/T 2038–2010 α-high-strength gypsum in China and have a good commercial application prospect. Moreover, in the phosphoric acid solution, the average diameter of the α-HH crystal increased from 8.1 µm to 54.8 µm, the average aspect (L/D) ratio decreased from 32.65 to 0.52, and the induction period and growth period of the α-HH crystal were prolonged with the increase in regulator dosage. F− and Al3+ ions were preferred to adsorb on the crystal faces. The growth of the crystal parallel to c-axis (200), (020), and (400) was inhibited, and the morphology of the α-HH crystal changed from whisker to short column. When the dosage of the regulator was 1.1 %, the 2 h bending strength of the α-HH product was 6.56 MPa, and the drying compressive strength was 52.4 MPa. This study provides a new technique and method for the synthesis of high-strength α-HH products from PG.

Preparation of α-hemihydrate gypsum whiskers from phosphogypsum using atmospheric pressure nitrate solution

Preparation of α-hemihydrate gypsum from phosphogypsum in glycerol and Na2SO4 mixed solutions under atmospheric pressure

Facile preparation of α-calcium sulfate hemihydrate whisker from by-product gypsum in chloride-free salt solution system

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Utilization of phosphogypsum to synthesize α-hemihydrate gypsum in H3PO4–H2O solution

Efficient removal of impurities from phosphogypsum during preparation of α-hemihydrate gypsum

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum

High efficient utilization of phosphogypsum:preparation and application of calcium sulfate whiskers

Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gas-desulfurization gypsum solid waste

Efficient precipitation of soluble phosphorus impurities in the recycling of phosphogypsum to produce hemihydrate gypsum

Effect of mixed cation acetate electrolyte on synthesis of α‐hemihydrate gypsum from phosphogypsum

A Simple and Efficient Method for Preparing High-Purity α-CaSO4·0.5H2O Whiskers with Phosphogypsum

Recycling of waste gypsum from αlpha-hemihydrate phosphogypsum: Based on the atmospheric hydrothermal process

Preparation of α-hemihydrate gypsum from phosphogypsum in recycling CaCl2 solution

The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Optimization of wet-process phosphoric acid for high-quality phosphogypsum

Insights into the Role of Na+ on the Transformation of Gypsum into Α-Hemihydrate Whiskers in Alcohol–Water Systems

The Optimal Conditions of Preparation of Phosphogypsum-Based Calcium Sulfate Hemihydrate Whiskers by Hydrothermal Method Using Phosphogypsum

Preparation of gypsum with high purity and whiteness from phosphogypsum for CO2 mineral sequestration