Abstract:Phosphogypsum (PG) is a solid waste generated during the wet production of phosphoric acid, noted for causing significant environmental pollution due to low pH and contamination with phosphorus-fluorine impurities. This work proposes an innovative method of acid treatment to acidify PG by directly adding of sulfuric acid at suitable temperatures. Initially, this acid treatment process is employed to convert and remove phosphorus-fluorine impurities, followed by PG after acid treatment incorporation with lime for safe solidification. The conversion mechanisms of phosphorus-fluorine impurities during acidification and solidification are elucidated. Results demonstrate that the direct acidification method converts most fluoride into H 2 SiF 6 and HF, which are subsequently released from the PG system after a temperature of 175 °C treatment. Phosphorus is wholly transformed into water-soluble forms (H 3 PO 4 /H 2 PO 4 - /HPO 4 2- ), especially as eutectic phosphorus is released and converted when CaSO 4 ·2 H 2 O crystals dissolve to II-CaSO 4 . Following acidification to achieve a high water-soluble phosphorus/fluorine ratio, lime is added to convert phosphorus-fluorine impurities into Ca 5 (PO 4 ) 3 F, ensuring harmlessness. The addition of 3.7 % lime to acidified PG, an acid amount of 2-times the theoretical requirement, yields a treatment solution with pH=8.65, ρ(P)=0.05 mg/L and ρ(F - )=1.11 mg/L, meeting Class V water discharge standards (GB 3838–2002). The solidified PG filter residue contains the water–soluble ω(P 2 O 5 ) ≤ 0.01 % and ω(F - ) ≤ 0.0061 %, suitable for safe storage. This work indicates that this process can separate phosphorus impurities with lower energy consumption, providing a harmless PG treatment. Furthermore, the treated PG can hydrate to gain strength, potentially enhancing its utility as a resource.

Preparation of gypsum with high purity and whiteness from phosphogypsum for CO2 mineral sequestration

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Study on Mechanisms for Improving Quality and Whiteness of Phosphogypsum Based on Process Mineralogy Analysis

Efficient extraction of impurities from phosphogypsum during crystal regulation of α‐hemihydrate gypsum

Gradient removal of Si and P impurities from phosphogypsum and preparation of anhydrous calcium sulfate

Efficient precipitation of soluble phosphorus impurities in the recycling of phosphogypsum to produce hemihydrate gypsum

Efficient removal of impurities from phosphogypsum during preparation of α-hemihydrate gypsum

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Utilization of Phosphogypsum to Prepare High-Purity CaCO 3 in the NH 4 Cl–NH 4 OH–CO 2 System

A Novel Process to Recover Gypsum from Phosphogypsum

Influence of Impurities on the Process of Obtaining Calcium Carbonate during the Processing of Phosphogypsum

Simultaneous removal of phosphorus and organic contaminants from phosphogypsum using hydrothermal method for gypsum resource regeneration

Preparation of Calcium Oxide by Decomposition of Phosphogypsum under CO and Water Vapor Atmosphere

Comparative analysis of colloid-mechanical microenvironments on the efficient purification of phosphogypsum

The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Research on the technology and mechanism of direct acidification of phosphogypsum and deeply solidify impurities with lime

Staged purification of phosphogypsum using pH-dependent separation process

Investigating the novel process for thorough removal of eutectic phosphate impurities from phosphogypsum

Characteristic pollutant purification analysis of modified phosphogypsum comprehensive utilization