Mechanical Behavior and Failure Mechanism of Three-Dimensional Braided Composites at Different Temperatures
Weimin Jiang,Junmeng Zhou,Jie Mei,Jiayi Liu,Wei Huang
DOI: https://doi.org/10.3139/120.111528
2020-01-01
Abstract:Abstract This investigation explored the effect of temperature on the compressive behaviors and failure mechanism of three dimensional (3D) carbon/ epoxy five-directional braided composite laminates. The compression tests of 3D braided composite laminates were performed at six different temperatures, which are 20 °C (room temperature), 50 °C, 70 °C, 90 °C, 110 °C and 130 °C, respectively. Then the effect of temperature on the failure mechanism, stress-strain curves, compressive modulus and strength of the composite laminates were analyzed and compared to that at room temperature. The results have shown that the temperature had a significant effect on the compressive properties and failure mechanism of 3D braided composite laminates. At 20 °C and 50 °C, the 3D braided composite laminates failed by shear fracture, and the stress-strain curves exhibited obvious linear elasticity and a brittle failure feature. While, at higher temperatures (70 °C, 90 °C, 110 °C and 130 °C), it was found that the specimens exhibited obvious plastic kinking, and the stress-strain curves exhibited obvious non-linear trend and a plastic failure feature due to the epoxy resin matrix becoming softened and plastic. The compressive modulus and strength decreased as temperature increased. The compressive modulus and strength decreased by 92.3 % and 93.8 % when the temperature increased from 20 °C to 130 °C.