Abstract:Carbon fiber reinforced polymer (CFRP) composites are commonly used for reflectors of artificial satellites operating in low earth orbit (LEO). The decay of the modulus of the CFRP composite varies under different thermal cycling environments, which can lead to a reduction in the accuracy of the reflector panels, affecting the transmission of signals. This paper investigates the impact of different thermal cycling conditions on the mechanical behavior of carbon fiber/epoxy laminated composites experimentally. Three kinds of thermal cycling conditions involving continuous temperature changes are employed to explore the influence of temperature range on the residual tensile and in-plane shear moduli of the laminates. Test results indicate that the upper temperature limit and the temperature span of the thermal cycling conditions jointly affect the mechanical properties of CFRP composite laminates, but the responses of the residual tensile and in-plane shear moduli are different under the variation of each temperature parameter alone. The residual tensile and in-plane shear moduli of the laminates under thermal cycling decrease with an expansion of the temperature span having the same upper limit. If the temperature span remains constant, an increase in the upper temperature limit leads to an increase in the residual tensile modulus, but a decrease in the residual in-plane shear modulus. The main damages causing the decay of residual tensile and in-plane shear moduli of unidirectional laminates were investigated by scanning electron microscopy (SEM) technology. Observations of the microscopic fracture of the material show that the post-curing reaction factor predominantly influences the residual tensile modulus of unidirectional laminates, while the fiber/matrix interface damage factor dominates the residual in-plane shear modulus of the unidirectional laminates. Furthermore, an increase in the fiber tensile modulus decreases both residual tensile and residual in-plane shear moduli. Notably, the residual in-plane shear modulus exhibits greater sensitivity to thermal cycling compared to the residual tensile modulus. The findings reported in this paper would provide valuable insights and guidance for the design and application of carbon fiber/epoxy composites subjected to thermal cycling conditions.

Cryogenic damage behavior of carbon fiber reinforced polymer composite laminates via fiber-optic acoustic emission

Damage evolution characterization of glass fabric composites at cryogenic temperatures via in-situ tensile X-ray computed tomography tests

Mechanism of Matrix Influencing the Cryogenic Mechanical Property of Carbon Fibre Reinforced Epoxy Resin Composite

Internal shear damage evolution of CFRP laminates ranging from -100°C to 100°C using in-situ X-ray computed tomography

Revealing low temperature-mechanical coupling failure mechanisms in CFRP laminates with in-situ observations

Experimental and multiscale modeling investigations of cryo-thermal cycling effects on the mechanical behaviors of carbon fiber reinforced epoxy composites

In-line monitoring of cryogenic three-point bending test of fiber-reinforced composites using acoustic emission

Experimental investigations of impact behavior and milling performance of T700-CFRP under cryogenic conditions

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

Investigation on damage behaviors of carbon fiber‐reinforced nylon 6 thermoplastic composite laminates using acoustic emission and digital image correlation techniques

On the mechanical behavior of carbon fiber/epoxy laminates exposed in thermal cycling environments

Mechanism Analysis on Tensile Fracture Properties of Heterogeneous BFLAC at Cryogenic Temperature: Experimental Investigation and Mesoscale Simulation

Damage Monitoring of Regularly Arrayed Short-Fiber-Reinforced Composite Laminates under Tensile Load Based on Acoustic Emission Technology

Effect of temperature and moisture composite environments on the mechanical properties and mechanisms of woven carbon fiber composites

Study on Dynamic Mechanical Properties of Carbon Fiber-Reinforced Polymer Laminates at Ultra-Low Temperatures

Damage characterization of FRP embedded with different optical fibers under tensile load using acoustic emission and micrographic real-time inspection

Failure behavior and damage visualization of thick carbon/aramid hybrid woven composites under flexural loading conditions

Flexural progressive damage and failure behavior of carbon-aramid/epoxy hybrid woven composites

Raman mapping microspectroscopy of the effects of cryogenic cycling on the interfacial micromechanics of carbon fiber-reinforced polyimide composites

Fatigue behavior and failure mechanisms of 3D angle-interlock woven composite at room and cryogenic temperatures under bending

Temperature-dependent creep damage mechanism and prediction model of fiber-reinforced phenolic resin composites