Temperature dependence of τf and its origin in MgTiO3–CaTiO3 microwave dielectric composites

Shuang Yang,Lei Li,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.05.076

IF: 5.7

2022-10-01

Journal of the European Ceramic Society

Abstract:As a key parameter of microwave dielectric ceramics, τf is required to be near-zero and usually treated as a temperature-independent constant. However, the strong temperature dependence of τf was observed in (1-x)MgTiO3–xCaTiO3 composites and the constituting phases. Especially for the composite with x = 0.06 and a near-zero average τf (τf,W) of − 2.3 ppm/°C, the normalized resonant frequency (f0̃) first increased and then decreased with temperature, and τf decreased significantly from 8.6 ppm/°C at − 40°C to − 13.4 ppm/°C at 80 °C. The temperature dependence of τf could be evaluated by the average dτfdT, which decreased monotonically from − 0.0206 ppm/°C2 to − 3.442 ppm/°C2 with increasing x from 0 to 1. The undesired temperature dependence of τf should be common in microwave dielectric composites with near-zero τf,W, which was determined by the nonlinear coefficient b2 and −τf2 of the constituting phases, and expected to be suppressed by adopting suitable constituting phases with relatively low |b2| and |τf,W|.

materials science, ceramics