A2Zr2O7 (A = Nd, Sm, Gd, Yb) zirconate ceramics with pyrochlore-type structure for high-temperature negative temperature coefficient thermistor

Yige Wang,Bo Gao,Qian Wang,Xiaohui Li,Zhi Su,Aimin Chang
DOI: https://doi.org/10.1007/s10853-020-05104-5
IF: 4.5
2020-08-24
Journal of Materials Science
Abstract:The aim of this paper is to present a novel negative temperature coefficient (NTC) thermistor based on A2Zr2O7 (A = Nd, Sm, Gd, Yb) zirconate ceramics with pyrochlore-type structure for high-temperature application. The zirconate ceramics were synthesized via a solid-state reaction method where rare-earth oxides and ZrO2 were used as starting materials. The physical structures were characterized by X-ray diffraction, scanning electron microscopy, and Raman spectroscopy. It was confirmed that Nd2Zr2O7 and Sm2Zr2O7 are pyrochlore phases, while Yb2Zr2O7 and Gd2Zr2O7 are defect fluorite phases. The electrical property investigated by using resistance–temperature measurements demonstrated that the prepared A2Zr2O7 zirconate ceramics exhibit a typical characteristic of NTC over a wide temperature range between 673 and 1273 K. Particularly, A2Zr2O7, in addition to having high activation energy to ensure better sensitivity, can still maintain higher resistivity under high-temperature environments. Furthermore, the resistivity of A2Zr2O7 is almost independent of the change in oxygen partial pressure. These properties are superior to the classical spinel-type or perovskite-type NTC thermistor, providing valuable information to explore new NTC thermistor for high-temperature applications.
materials science, multidisciplinary
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop new negative temperature coefficient (NTC) thermistor materials suitable for high - temperature environments. Specifically, the authors hope to find an NTC thermistor material that can still maintain high stability and sensitivity under high - temperature conditions, in order to meet the needs of high - precision sensing, monitoring and control systems in fields such as automotive electronics, military, and aerospace. ### Problem Background Traditional NTC thermistor materials, such as materials based on transition - metal - oxide solid solutions (Mn, Co, Ni, Fe, Cu and Zn), become unstable at temperatures exceeding 300 °C, and their electrical properties also change. Therefore, it is particularly important to explore new NTC thermistor materials that can work at higher temperatures. ### Research Objectives This paper aims to introduce a new NTC thermistor material based on A₂Zr₂O₇ (A = Nd, Sm, Gd, Yb) zirconate ceramics with a pyrochlore structure. This material has the following characteristics: 1. **NTC characteristics in a wide temperature range**: It exhibits typical NTC characteristics in the temperature range from 673 K to 1273 K. 2. **High activation energy**: Ensures better temperature sensitivity. 3. **High resistivity**: Can maintain a relatively high resistivity even in a high - temperature environment. 4. **Insensitivity to changes in oxygen partial pressure**: The resistivity is hardly affected by changes in oxygen partial pressure. These characteristics make A₂Zr₂O₇ zirconate ceramics more advantageous than classical spinel - type or perovskite - type NTC thermistor materials, providing valuable information for the research of high - temperature NTC thermistor materials. ### Conclusions The A₂Zr₂O₇ (A = Nd, Sm, Gd, Yb) zirconate ceramics prepared by the solid - phase reaction method exhibit typical NTC characteristics in the temperature range from 673 K to 1273 K. In addition, these materials can still maintain a high resistivity in a high - temperature environment, and the resistivity is hardly affected by changes in oxygen partial pressure. These excellent properties provide an important reference for the development of new high - temperature NTC thermistor materials.