Synthesis of YCrO 3 ceramics through a field-assisted sintering technique

Bo Zhang,Qing Zhao,Aimin Chang,Yin Liu,Yiyu Li,Yiquan Wu

DOI: https://doi.org/10.1007/s10854-014-1741-5

2014-01-01

Abstract:The YCrO 3 negative temperature coefficient (NTC) ceramics have been successfully fabricated through a field-assisted sintering technique with a low sintering temperature and a short sintering period. The orthorhombic perovskite YCrO 3 powder synthesized from a Pechini method was formed at a temperature range of 780–800 °C through a decomposition of YCrO 4 . The as-sintered YCrO 3 ceramics had a relative density of 97.6 %. The values of ρ 25 , ρ 600 , B 25/600 and activation energy of the YCrO 3 NTC thermistor were 1.21 × 10 6 Ω cm, 7.26 × 10 2 Ω cm, 3,358 K, 0.293 eV, respectively. Such ceramics could be used as the potential candidates for NTC thermistors in a wide temperature range from 25 to 600 °C.