Flexible Hard Coatings with Self-Evolution Behavior in a Low Earth Orbit Environment
Dan Wang,Jusha Ma,Pengfei Li,Lin Fan,Yuemin Wu,Zongbo Zhang,Caihong Xu,Lei Jiang
DOI: https://doi.org/10.1021/acsami.1c13807
2021-09-17
Abstract:Lightweight, long lifetime, and flexible polymer membrane-based structures, which are tightly folded on the ground and then unfolded in space, suffer from repeated bending before launching and fatal erosion on exposure to atomic oxygen (AO) in a low Earth orbit (LEO). Although various AO-resistant coatings have been developed, a coating that can simultaneously meet the critical requirements for the mechanical robustness and long-term protection of polymer membranes is rare. Here, we fabricated a coating with mechanical robustness and long-term space endurance, starting from an inorganic polymer precursor. A hybrid coating with a nanoscale polymer/silica bicontinuous phase is first prepared on the ground, which exhibits outstanding flexibility and excellent abrasion resistance. Then, the coating shows an in situ self-evolution behavior under AO and ultraviolet (UV) synergism to afford dense and crack-free silica coating with outstanding endurance. Our strategy displays great potential for protecting deployable membrane structures serving in the LEO.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c13807.Abbreviation of hybrid coatings; transmittance, SEM and AFM, hydrolysis and condensation reactions, Si 2p spectra, IR absorbance intensities of hybrid coatings; the alkali etching test of hybrid coatings; SEM and nanoindentation curves of PHPS/SiO2 composite coatings; XPS spectra and element composition of PI, PI with ca. 10 nm thick CH150 and with ca. 570 nm thick CH150; bending tests; 3H scratch resistance; wear tests; mechanical properties of PI with hybrid coatings; and IR spectra, SEM, AFM, density, nanoindentation, XPS depth profiles, ESR, transmittance, and adhesion of hybrid coatings after UV and AO radiation (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology