Electrochemical Polishing of Ti and Ti6Al4V Alloy in Non-Aqueous Solution of Sulfuric Acid

Agata Kołkowska,Joanna Michalska,Rafał Zieliński,Wojciech Simka

DOI: https://doi.org/10.3390/ma17122832

IF: 3.4

2024-06-11

Materials

Abstract:This paper reports the results of our study on electrochemical polishing of titanium and a Ti-based alloy using non-aqueous electrolyte. It was shown that electropolishing ensured the removal of surface defects, thereby providing surface smoothing and decreasing surface roughness. The research was conducted using samples made of titanium and Ti6Al4V alloy, as well as implant system elements: implant analog, multiunit, and healing screw. Electropolishing was carried out under a constant voltage (10–15 V) with a specified current density. The electrolyte used contained methanol and sulfuric acid. The modified surface was subjected to a thorough analysis regarding its surface morphology, chemical composition, and physicochemical properties. Scanning electron microscope images and profilometer tests of roughness confirmed significantly smoother surfaces after electropolishing. The surface profile analysis of processed samples also yielded satisfactory results, showing less imperfections than before modification. The EDX spectra showed that electropolishing does not have significant influence on the chemical composition of the samples.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

### Problems Addressed by the Paper

The paper primarily investigates the effectiveness of electrochemical polishing of titanium (Ti) and its alloy Ti6Al4V in non-aqueous solutions. Specifically, the study aims to improve the smoothness of the surface of titanium and its alloys through electrochemical polishing and reduce surface roughness, thereby enhancing their performance as dental implant materials.

#### Main Objectives:
1. **Surface Defect Removal**: Remove surface defects of titanium and its alloys through electrochemical polishing techniques.
2. **Surface Smoothness Improvement**: Ensure that the polished surface is smoother, reducing surface roughness.
3. **Chemical Composition Retention**: Minimize changes to the material's chemical composition during the polishing process.
4. **Corrosion Resistance Enhancement**: Reduce bacterial adhesion through surface treatment, thereby improving the material's corrosion resistance.
5. **Electrolyte Formula Optimization**: Use a non-aqueous solution of methanol and sulfuric acid as the electrolyte to avoid the formation of a stable oxide layer and improve polishing effectiveness.

#### Experimental Methods:
- **Sample Preparation**: Use pure titanium (Grade 4) and Ti6Al4V alloy (Grade 5) as experimental samples, including various components of the dental implant system.
- **Electrochemical Polishing Process**: Conduct electrochemical polishing at a constant voltage (10-15 V) with an 8% sulfuric acid methanol solution as the electrolyte.
- **Characterization Analysis**: Analyze the surface morphology and chemical composition of the samples using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDX), and measure surface roughness with a profilometer.

#### Results and Discussion:
- **Surface Morphology**: SEM images show that electrochemical polishing significantly reduces surface defects, making the surface smoother.
- **Chemical Composition**: EDX analysis indicates that the chemical composition of the material remains largely unchanged after polishing, with no contaminants from the electrolyte detected.
- **Roughness**: Surface roughness is significantly reduced, with samples treated at 12.5 V showing the best performance.
- **Contact Angle**: Although the changes in contact angle are complex, overall, the polished surface exhibits better wettability.

In summary, the paper experimentally verifies the effectiveness and safety of using sulfuric acid and methanol as electrolytes for electrochemical polishing in non-aqueous solutions, providing a new surface treatment method for titanium and its alloys in dental implant applications.