Abstract:Poly(lactic acid) (PLA) was an eco‐friendly and biodegradable material. However, its molecular chain was inflexible and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness of PLA. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were formed between hydroxyl groups on EHBP and PLA, and the combined action of the two ultimately improved the toughness and strength of PLA. Chemical micro‐crosslinking was validated via Fourier transform infrared spectroscopy (FTIR) and gel content analysis. By observing the microscopic morphology of the impact fracture of the blends, it was found that the interface adhesion of the blends increased with the addition of EHBP, enhancing the corresponding mechanical properties. The best interface adhesion was achieved when 2.5 phr EHBP was added to PLA. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8% respectively, achieving the goal of simultaneously enhancing the toughness and strength of PLA. The simultaneous improvement in the strength and toughness of PLA expands its potential application value. Poly(lactic acid) (PLA) is an eco‐friendly and biodegradable material. However, its molecular chain was rigid and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were also formed between EHBP and PLA. The combined action of the above two aspects ultimately improved the toughness and strength of PLA. The mechanical property tests results showed that the mechanical properties of PLA improved best when 2.5 phr of EHBP was added. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8%, respectively, compared to those of neat PLA. It achieves the goal of simultaneously enhancing the toughness and strength of PLA and subsequently expands its potential application applications.

Effect of oligomers from epoxidized soybean oil and sebacic acid on the toughness of polylactic acid /bamboo fiber composites

Toughness Enhancement of Poly(lactic Acid), Bamboo Particle and Ultrafine Bamboo-Char Ternary Biocomposites by Polyethylene Glycol Plasticization

Improved properties of PLA biocomposites toughened with bamboo cellulose nanowhiskers through silane modification

Preparation and Characterization of Maleic Anhydride Compatibilized Poly(lactic acid)/Bamboo Particles Biocomposites

Fiber treatment impact on toughness and interfacial bonding in epoxidized soya bean oil compatibilized PLA/PBAT bamboo fiber composites

Cardanol derivatives as compatibilizers for strengthening and toughening polylactic acid/bamboo fiber bio‐composites

Sustainable improvement in the polylactic acid properties of 3D printing filaments: The role of bamboo fiber and epoxidized soybean oil‐branched cardanol ether compatibilizer

Epoxidized Soybean Oil Toughened Poly(lactic acid)/Lignin-g-Poly(lauryl methacrylate) Bio-Composite Films with Potential Food Packaging Application

Waste Cellulose Fibers Reinforced Polylactide Toughened by Direct Blending of Epoxidized Soybean Oil

Improvement of Compatibility and Mechanical Performances of PLA/PBAT Composites with Epoxidized Soybean Oil as Compatibilizer

Influence of bio-coupling agent on interfacial interlocking compatibility and toughness of ultrafine bamboo charcoal/polylactic acid composite film

The Consequence of Epoxidized Soybean Oil in the Toughening of Polylactide and Micro-Fibrillated Cellulose Blend

Poly(l-lactide)/poly(d-lactide)/bamboo fiber (BF) bio-composites with enhanced heat resistance, mechanical and rheological performance

Toughening Polylactide with Epoxidized Styrene–butadiene Impact Resin: Mechanical, Morphological, and Rheological Characterization

Research on Toughening Polylactic Acid by an Epoxy Soybean Oil Curing Network Based on Dynamic Cross-Linking

Improving the Performance of Polylactic Acid/polypropylene/cotton Stalk Fiber Composites with Epoxidized Soybean Oil As a High Efficiency Plasticizer.

Enhancement of the Mechanical Properties of Poly(lactic Acid)/epoxidized Soybean Oil Blends by the Addition of 3-Aminophenylboronic Acid.

Construction of Cross-Linked Networks in Polylactic Acid Biocomposites by Using Vegetable Oil-Modified Collagen Fibers for Improving Anti-Stress Relaxation and Toughness

Synergistic toughening and reinforcement of poly(lactic acid) with epoxy‐terminated hyperbranched polymers

Interfacial interaction improvement of polylactic acid/bamboo-char biocomposites for high toughness, good strength, and excellent thermal stability

Strong and Tough Polylactic Acid Based Composites Enabled by Simultaneous Reinforcement and Interfacial Compatibilization of Microfibrillated Cellulose