Abstract:Polyvinyl chloride (PVC) is the most widely used general flame-retardant plastic worldwide; however, the large number of plasticizers added during processing significantly reduces its flame-retardant property. To prepare a new type of PVC material with highly efficient flame retardancy and smoke suppression, antimony trioxide (Sb2O3), talc powder, hydromagnesite, and zinc borate were added in different proportions to PVC to explore the flame-retardant properties, thermal weight, smoke density (Ds), and mechanical properties of the composite materials. Results showed that the limiting oxygen index value of each group was higher than 27% after adding talc powder, magnesite, and zinc borate to replace part of the Sb2O3. This value was within the refractory-grade level and indicated a good flame retardancy performance. The replacement effect was in line with the experimental expectation. The lowest Ds peak value was 656.4 when the flame retardants were added with 10 wt% Sb2O3, 50 wt% hydromagnesite, 20 wt% talc, and 20 wt% Zn3BO6. Compared with pure Sb2O3 as a flame retardant, the Ds peak value decreased by 46.7%. The thermogravimetric decomposition temperature of the composites in each group was generally higher than that of the group with pure Sb2O3 as a flame retardant, increasing by 45.3 °C. The thermal stability of the composites was improved, and the elongation at the break and tensile strength were 234.9% and 25.8 MPa, respectively, indicating good mechanical properties. The results showed that using compound flame retardants to replace most of the Sb2O3 is an effective technique for obtaining good flame retardancy and mechanical properties of PVC. This study, not only reduced the manufacturing cost of flame-retardant PVC, but also effectively reduced its smoke density and the time to reach the highest smoke density, which provided a research reference for the application and promotion of flame-retardant PVC.

Bismuth trioxide replaced diantimony trioxide to obtain polyvinyl chloride leather with high flame retardancy and low flame propagation rate

Biomimetic Synthesis of Zinc Hydroxystannate-Coated Calcium Carbonate and Its Application in PVC

A Novel Halogen‐free Intumescent Flame Retardant Containing Phosphorus and Nitrogen and Its Application in Polypropylene Systems

Study on Controlled Synthesis of Zinc Carbonate Via Mixed Template and Hydroxystannate-coated Calcium Its Flame Retardancy in PVC

Enhanced flame retardancy and thermal stability of zinc borate and magnesium carbonate as a promising alternative for Sb2O3 toward polyvinyl chloride

The Flame Retardancy and Smoke Suppression Performance of Polyvinyl Chloride Composites with an Efficient Flame Retardant System

Improving the flame retardancy and smoke suppression of flexible PVC by incorporating zinc borate‐modified diantimony trioxide

Simultaneously enhanced flame retardancy and smoke suppression properties of flexible polyvinyl chloride with the incorporation of modified Mg(OH) 2 and Sb 2 O 3

Effects of Chlorinated Polyethylene and Antimony Trioxide on Recycled Polyvinyl Chloride/acryl-Butadiene-styrene Blends: Flame Retardancy and Mechanical Properties

Preparation of Pillared Layered Antimony Hydroxide and Its Flame Retardancy in Thermoplastic Polyurethane

Bismuth Subcarbonate Nanoplates for Thermal Stability, Fire Retardancy and Smoke Suppression Applications in Polymers: A New Strategy

Synthesis of Core/Shell Structured Zinc Borate/Silica and Its Surface Charring for Enhanced Flame Retardant Properties

Preparation of Zinc Hydroxystannate Coated Dendritic-Fibrillar Barium Carbonate and Its Flame Retardant Effect on Soft Poly (vinyl Chloride)

Synthesis of Brominated Flame Retardants with Different Brominated Structures and Study on Flame Retardancy of Polystyrene Resin

Synergistic Flame Retardancy of Linear Low-Density Polyethylene with Surface Modified Intumescent Flame Retardant and Zinc Borate

To improve the flame retardancy, mechanical properties and degradation rate of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) by divinybenzene-maleic anhydride microsphere

An Overview of the Flame Retardants for Poly(vinyl chloride): Recent States and Perspective †

RETRACTED ARTICLE: Preparation of Multilayers Zinc Hydroxystannate Microcapsules and its Application in Flame-Retardant PVC Composites

The improvement of flame retardancy and compatibility of PBAT/PLLA via a hybrid polyurethane

Reinforcing Condensed Phase Flame Retardancy through Surface Migration of Brucite@Zinc Borate-Incorporated Systems

The effects of zinc hydroxystannate/boron nitride hybrids and aluminum diethylphosphinate on flame retardancy and smoke suppression of styrene–butadiene rubber composites