Abstract:Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) (P34HB), as a bio-originated and biodegradable polyester, is expected to be developed to substitute traditional petroleum-based plastics. However, its flammability restrains its application, intumescent flame retardant (IFR) has been used in P34HB. Herein, a rigid microsphere divinylbenzene-maleic anhydride (DM) copolymer was used as a synergistic agent with IFR together in P34HB. The LOI of the 83wt% P34HB/16wt% IFR/1wt% DM reached 30.0%, and the composite also passed the UL-94 V-0 rating. In the cone calorimeter test, the peak heat release rate (PHRR) of the control P34HB was 727 kW/m 2 , which was reduced to 281 kW/m 2 for the 83wt% P34HB/16wt% IFR/1wt% DM. The total smoke production (TSP) of the control P34HB was 12.1 m 2 , however, the TSP value of 83wt% P34HB/16wt% IFR/1wt% DM was reduced to 8.4 m 2 . The results showed that DM acted as an ideal synergist flame retardant. For the 75wt% P34HB/25wt% IFR, the tensile strength and impact strength were 13.7 MPa and 4.2 KJ/m 2 , respectively and for the 83wt% P34HB/16wt% IFR/1wt% DM, they were increased to 18.1 MPa and 9.1 KJ/m 2 , respectively. In the degradation process, the weight loss rate of control P34HB was 0.1 mg/h, and that was 0.56 mg/h for 83wt% P34HB/16wt% IFR/1wt% DM, which indicated that the IFR/DM accelerated the degradation of P34HB. All the work documented that DM improved the flame retardant, mechanical properties, and degradation rate of P34HB.

To improve the flame retardancy, mechanical properties and degradation rate of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) by divinybenzene-maleic anhydride microsphere