High-Temperature Mass Spectrometric Study of the Vaporization of Oxycarbide MAX Phase Ceramics

V. A. Vorozhtcov,V. L. Stolyarova,S. I. Lopatin,A. L. Shilov

DOI: https://doi.org/10.1134/s0036023623603045

2024-07-19

Russian Journal of Inorganic Chemistry

Abstract:The vaporization of the carbide materials with the chemical compositions Ti 2 SiC, Ti 3 SiC 2 , Ti 2 AlC, Ti 3 AlC 2 , Zr 2 AlC, and Zr 3 AlC 2 containing MAX phases and of oxycarbide systems based on these materials with hafnia additives was examined by Knudsen effusion mass spectrometry at temperatures up to 2200 K. Atomic aluminum was identified as the major vapor species over the Ti 2 AlC, Ti 3 AlC 2 , Zr 2 AlC, and Zr 3 AlC 2 samples at 1500 K. The silicon-containing samples were less volatile than the aluminum-containing carbide materials; they vaporized observably at temperatures above 1900 K to form Si, Si 2 , SiC 2 , and Si 2 C vapor species. The addition of hafnia to the carbides under study led to the formation of oxygen-containing vapor species, particularly Al 2 O and SiO, and to a decrease in total vapor pressure over the systems formed. The least volatile materials were samples of the Ti 2 SiC–HfO 2 oxycarbide system, and among the aluminum-containing oxycarbide systems, samples of the Zr 2 AlC–HfO 2 system containing up to 10 mol % hafnia and samples of the Ti 2 AlC–HfO 2 system with a higher HfO 2 content.

chemistry, inorganic & nuclear