Simultaneously improving piezoelectric properties and temperature stability of Na0.5K0.5NbO3 (KNN)-based ceramics sintered in reducing atmosphere

Zhenyong Cen,Shuaishuai Bian,Ze Xu,Ke Wang,Limin Guo,Longtu Li,Xiaohui Wang
DOI: https://doi.org/10.1007/s40145-021-0475-0
IF: 11.534
2021-07-13
Journal of Advanced Ceramics
Abstract:Abstract It is a very difficult work to sinter K 0.5 Na 0.5 NbO 3 (KNN)-based materials with good reduction resistance in strong reducing atmosphere. 0.945K 0.48 Na 0.52 Nb 0.96 Ta 0.04 O 3 −0.055BaZrO 3 + 0.03ZrO 2 + y mol%MnO (KNNT−0.055BZ + 0.03Zr + y Mn) ceramics sintered in reducing atmosphere were prepared successfully by conventional solid-state reaction methods. MnO dopant increases grain size at y = 5–8 due to strong lattice distortion and then decreases grain size at y = 9 due to much Mn 4 Nb 2 O 9 accumulated at the grain boundary. MnO dopant as an excellent sintering aid can effectively reduce volatilization of alkali metal by decreasing the sintering temperature ( T sinter ). Reducing alkali metal volatilization can greatly reduce oxygen vacancies and improve piezoelectric properties. MnO dopant can improve the anti-reduction properties. The KNNT−0.055BZ + 0.03Zr + y Mn ceramics at y = 6–9 show outstanding anti-fatigue of unipolar piezoelectric strain under the synergistic effect of reduced oxygen vacancies due to reduced volatilization and increased grain size. Piezoelectric properties and temperature stability of KNNT−0.055BZ + 0.03Zr ceramics sintered in reducing atmosphere are improved simultaneously by MnO dopant. Optimum inverse piezoelectric coefficient ( d 33 * ) of ceramics at y = 8 reaches up to 480 pm/V under low driving electric field E = 20 kV/cm at room temperature, and its temperature stability of d 33 * reaches 158 °C. It will be an excellent lead-free material candidate for the preparation of multilayer piezoelectric actuators co-fired with nickel electrode.
materials science, ceramics
What problem does this paper attempt to address?
The main problem this paper attempts to address is the improvement of the piezoelectric performance and temperature stability of lead-free piezoelectric ceramic materials Na0.5K0.5NbO3 (KNN)-based ceramics when sintered in a reducing atmosphere. Specifically, the researchers aim to achieve this goal by doping MnO into KNN-based ceramics, with the objective of reducing the formation of oxygen vacancies, enhancing fatigue resistance, and improving temperature stability. ### Main Issues: 1. **Improving Piezoelectric Performance**: The piezoelectric performance of KNN-based ceramics still lags behind lead-containing ceramics, especially in multilayer piezoelectric actuator applications. By doping MnO, the researchers hope to increase the piezoelectric coefficient (d33) of KNN-based ceramics. 2. **Enhancing Temperature Stability**: The performance stability of KNN-based ceramics at high temperatures is relatively poor, which limits their use in practical applications. The researchers aim to improve the temperature stability of the material by doping MnO. 3. **Enhancing Fatigue Resistance**: KNN-based ceramics tend to exhibit performance degradation, or fatigue, after prolonged use. The researchers hope to improve the fatigue resistance of the material by reducing the formation of oxygen vacancies. ### Solutions: - **Doping MnO**: MnO, as a sintering aid, can effectively lower the sintering temperature (Tsinter), thereby reducing the volatilization of alkali metals and subsequently decreasing the formation of oxygen vacancies. - **Optimizing Sintering Process**: By controlling the sintering temperature and atmospheric conditions, the researchers were able to successfully prepare KNN-based ceramics with good performance in a reducing atmosphere. ### Experimental Results: - **Piezoelectric Performance**: The MnO-doped KNN-based ceramics exhibited optimal inverse piezoelectric coefficient (d33*) of 480 pm/V at y = 8, and good temperature stability at low driving electric field (E = 20 kV/cm), with temperature stability reaching 158 ℃. - **Fatigue Resistance**: The MnO-doped KNN-based ceramics showed excellent unipolar piezoelectric strain fatigue resistance (β > 94%) at y = 6–9, attributed to the synergistic effect of reduced oxygen vacancies and increased grain size. ### Conclusion: By doping MnO, the researchers successfully improved the piezoelectric performance, temperature stability, and fatigue resistance of KNN-based ceramics, making them an ideal candidate for the preparation of multilayer piezoelectric actuators. These improvements provide significant technical support for the promotion of KNN-based ceramics in practical applications.