Photooxidative degradation and fragmentation behaviors of oriented isotactic polypropylene

Yingjun An,Tomoko Kajiwara,Adchara Padermshoke,Thinh Van Nguyen,Sinan Feng,Hiroyasu Masunaga,Yutaka Kobayashi,Hiroshi Ito,Sono Sasaki,Atsuhiko Isobe,Atsushi Takahara

DOI: https://doi.org/10.1038/s41428-023-00876-4

IF: 3.135

2024-01-25

Polymer Journal

Abstract:The photooxidative degradation and fragmentation behaviors of isotactic polypropylene ( it PP) were simulated in laboratory after various postconditions, such as quenching, gradual cooling and drawing, using an artificial weathering machine and a blender. The crystallinity of the it PP films and orientation of the molecular chains play important roles in the photooxidation of the it PP films. Compared to quenched it PP films with the same ultraviolet (UV) exposure time, highly oriented it PP films and gradually cooled it PP films with higher crystallinity exhibited a lower rate of photooxidative degradation. To clarify the photooxidative degradation mechanism, the surface morphology, chemical structure, and microstructure of the UV-exposed it PP films were investigated using scanning electron microscopy, infrared spectroscopy, differential scanning calorimetry, and wide- and small-angle X-ray scattering. Photooxidative degradation was inhibited as the orientation degree of the it PP film increased. These results indicate that photooxidation likely occurs in the amorphous phase of it PP. Oriented molecular chains effectively slowed the photooxidative degradation of the it PP films. The artificial fragmentation test of UV-exposed it PP films showed that it PP films with lower crystallinity and orientation degrees were crushed into microplastics that were much smaller in size than those with higher crystallinity or orientation degrees.

polymer science