Programming Crystallographic Orientation in Additive‐Manufactured Beta‐Type Titanium Alloy

Xuan Luo,Tao Song,Annett Gebert,Kai Neufeld,Ivan Kaban,Hongwei Ma,Weisi Cai,Haizhou Lu,Dongdong Li,Ning Li,Yuanyuan Li,Chao Yang
DOI: https://doi.org/10.1002/advs.202302884
IF: 15.1
2023-07-30
Advanced Science
Abstract:A technique of multi‐track coupled directional solidification (MTCDS) to program the orientation along an arbitrary 3D direction is established in additively manufactured β‐Ti alloys. MTCDS can be achieved via directional solidification of coupled multi‐track melt pools with a specific temperature gradient direction. This technology provides a method to develop biomedical Ti alloys with low elastic modulus and other high‐performance metallic materials. Additively manufactured metallic materials typically exhibit preferential or crystallographic orientations along the build direction. Nowadays, the challenge is to program crystallographic orientation along arbitrary 3D direction in additive‐manufactured materials. In this work, it is established a technique of multitrack coupled directional solidification (MTCDS) to program the crystallographic orientation along an arbitrary 3D direction in biomedical beta‐type Ti‐Nb‐Zr‐Ta alloys via laser powder bed fusion (LPBF). MTCDS can be achieved via directional solidification of coupled multi‐track melt pools with a specific temperature gradient direction. This results in continuous epitaxial growth of the β‐Ti phase and consequently sets the crystallographic orientation along an arbitrary 3D direction. This way, relatively low elastic modulus values of approximately 60 ± 1.2 GPa are customized along an arbitrary 3D direction. It is expected that MTCDS can be generalized to a wide range of applications for programming specific crystallographic orientations and, respectively, tailoring desired properties of different metallic materials.
materials science, multidisciplinary,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?
### Problems the Paper Aims to Solve This paper aims to address the challenge of programming specific crystal orientations in metal materials in arbitrary three-dimensional directions through additive manufacturing technologies such as Laser Powder Bed Fusion (LPBF). Specifically, the researchers developed a Multi-Track Coupled Directional Solidification (MTCDS) technique to program <001> crystal orientations in β-type titanium alloys along arbitrary three-dimensional directions. ### Background and Motivation 1. **Crystal Orientation Issues in Additive Manufacturing**: - Metal materials produced by additive manufacturing typically exhibit <001> or <110> crystal orientations along the build direction. - The current challenge is to program crystal orientations in additive manufacturing materials along arbitrary three-dimensional directions. 2. **Limitations of Existing Methods**: - Existing additive manufacturing technologies mainly focus on the design of microstructures and the programmability of macroscopic properties, but have not fully utilized these capabilities to achieve the desired macroscopic properties. - Temperature gradient is a key factor in controlling the direction of crystal growth, but existing methods find it difficult to precisely control the temperature gradient to achieve specific crystal orientations. ### Solution 1. **Multi-Track Coupled Directional Solidification (MTCDS) Technique**: - By precisely controlling the temperature gradient direction of multiple melt pools, directional solidification and continuous epitaxial growth of crystals are achieved. - This technique can program <001> crystal orientations along arbitrary three-dimensional directions, thereby customizing the elastic modulus of the material. 2. **Experimental Validation**: - The effectiveness of the MTCDS technique was validated using β-type Ti-35Nb-7Zr-5Ta alloy as the research object. - Experimental results show that the MTCDS technique can achieve <001> crystal orientations in arbitrary three-dimensional directions, customizing the elastic modulus to approximately 60 ± 1.2 GPa. ### Application Prospects 1. **Biomedical Applications**: - Metal materials with low elastic modulus are very beneficial for reducing stress shielding effects, especially in the manufacture of bone implants. - The MTCDS technique can customize the elastic modulus along specific three-dimensional directions, better matching the mechanical properties of bone tissue and reducing the strain mismatch between the implant and bone tissue. 2. **Other Applications**: - This technique is expected to be extended to the additive manufacturing of a wider range of high-performance metal materials, achieving the programming of specific crystal orientations to customize the desired properties. ### Conclusion By developing the MTCDS technique, this paper successfully addresses the challenge of programming crystal orientations in arbitrary three-dimensional directions during the additive manufacturing process, providing a new method for customizing biomedical implants and other high-performance metal materials.