Abstract:Al2O3, as one of the gate dielectric materials for thin film transistors (TFTs), has been extensively investigated because of its large bandgap, high breakdown field, and good thermal stability. However, the further development of Al2O3 thin films is limited by the presence of defects such as oxygen vacancies, self-interstitial atoms, or impurity elements. To overcome this obstacle, we have developed a novel method for fabricating Al2O3 thin films by using the atomic layer deposition (ALD) technique. This method replaces the conventional Trimethylaluminium (TMA)/H2O cycles with TMA/TMA/H2O/H2O cycles (referred to as ‘double cycles’), to deposit the Al2O3. The 5-nm ultrathin Al2O3 film showed a high areal capacitance of 660 nF/cm2 at 20 Hz, and a relatively low current density of 10−8 A/cm2 at 1 MV/cm. InGaZnO (IGZO) TFTs with ultrathin Al2O3 gate dielectric grown by double cycles exhibited outstanding performances, such as a near theoretical limit subthreshold swing (SS) of 70 mV/decade, a higher on/off current ratio $(I_{\mathrm{ on}} / I_{\mathrm{ off}}$ ) of 106, an increased field-effect mobility ( $\mu $ ) of 6.5 cm2/Vs, a lower threshold voltage $(V_{\mathrm{ th}})$ of 0.2 V, and a low operating voltage of 3 V. These results are superior to the IGZO TFTs with Al2O3 dielectrics deposited using the single TMA/H2O cycle. Therefore, the implementation of ‘double cycles’ in the fabrication of dielectrics through ALD demonstrates considerable potential for future application in low-power electronic devices.

High performance IZO:P/IZO:Ni thin film transistor with double active layers

Influence of Double Channel Layers on the Performance of Nitrogen Doped Indium-zinc-oxide Thin Film Transistors

High-Performance Thin Film Transistor with an Neodymium-Doped Indium Zinc Oxide/Al2O3 Nanolaminate Structure Processed at Room Temperature

Amorphous indium zinc oxide thin film transistors with poly-4-vinylphenol gate dielectric layers

Fully transparent high performance thin film transistors with bilayer ITO/Al-Sn-Zn-O channel structures fabricated on glass substrate

Fabrication and performance of indium oxide based transparent thin film transistors

High mobility of IGO/IGZO double-channel thin-film transistors by atomic layer deposition

High‐Performance Thin‐Film Transistors with Nickel‐Doped Indium Zinc Oxide Channel Layers

P‐1.8: High Performance Amorphous IZO/IGZO Bilayer Thin Film Transistors for Ink‐jet Printed AMOLED Displays

Amorphous IZO-based transparent thin film transistors

Performance improvement of tin-doped zinc oxide thin-film transistor by novel channel modulation layer of indium tin oxide/tin zinc oxide

High-Performance Unannealed A-Ingazno Tft with an Atomic-Layer-Deposited Sio2 Insulator

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al₂O₃ Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

High-Performance Mo-Zn-O Oxide Transistors with Double Channels

High-performance Fully Transparent Al–Sn–Zn–O Thin-Film Transistors Using Double-Channel Structures

Performance Improvement of Amorphous Thin-Film Transistors with Solution-Processed InZnO/InMgZnO Bilayer Channels

High-Performance of InGaZnO TFTs With an Ultrathin 5-nm Al2O3 Gate Dielectric Enabled by a Novel Atomic Layer Deposition Method

P‐1.23: High‐Performance Dual‐Gate A‐igzo/a‐izo Thin‐Film Transistors

High-Performance Amorphous InGaZnO Thin-Film Transistor Gated by HfAlOₓ Dielectric with Ultralow Subthreshold Swing

Performance Enhancement for Indium-Free Metal Oxide Thin-Film Transistors with Double-Active-Layers by Magnetron Sputtering at Room Temperature

Enhancement in electrical properties of dual-active-layer amorphous SiZnSnO/SiInZnO thin film transistors