Abstract:Co-processing of industrial wastes as alternative raw materials in cement manufacture is an example of industrial symbiosis for improved material resource efficiency. Since co-processing introduces impurities from wastes, such as air pollution control residue (APCR) from municipal solid waste combustion, into the cement kiln, a better understanding of their environmental impacts and effects on cement manufacturing and quality is needed. Portland cement clinkers containing 5-35% raw or 5-34% washed APCR were prepared, with formation of all typical minerals, but with effects on clinkering reactions, and increased 2CaO center dot SiO2 and decreased 3CaO center dot SiO2 and 3CaO center dot Al2O3. Raw APCR affected the shape of the 2CaO center dot SiO2 and 3CaO center dot SiO2 grains, and cement paste from clinker made with 35% APCR exhibited negligible 28d strength. Pastes from the clinkers with lower contents of APCR or washed APCR had strengths that were lower than that of the control at 7d, similar at 28d (similar to 90 MPa) and higher at 6 m (up to 120 MPa), consistent with their 2CaO center dot SiO2 and 3CaO center dot SiO2 contents. Utilization of minerals in APCR thus comes with a trade-off against cement quality. Volatilisation of S, Cl, Pb was reduced by washing, which fully eliminated volatilisation of Zn. Zn was found mainly in the interstitial phases of the clinker, in solid solution in 4CaO center dot Al2O3 center dot Fe2O3 or 3CaO center dot Al2O3. Further investigation is required to determine whether Zn and other incorporated elements may be released from the cement paste when these phases react with water. APCR co-processing may reduce CO2 emissions by avoiding CaCO3 decomposition, but this is an uncertain benefit, which may be outweighed by the detrimental effects of APCR alkalis, Cl, S and metals on cement production and quality. Life cycle environmental impacts associated with washing, and dispersal of contaminants in the built environment through construction materials, are additional concerns. (C) 2020 Published by Elsevier Ltd.

Calcium carbonate and reactive silica recovery from waste cement: The influence of processing parameters on upcycled material properties and carbon intensity

Mechanism Underlying Early Hydration Kinetics of Carbonated Recycled Concrete Fines-Ordinary Portland Cement (CRCF-OPC) Paste

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Recycling of calcined carbonated cement pastes as cementitious materials: Proposed CCUS technology for calcium looping

Co-processing of Raw and Washed Air Pollution Control Residues from Energy-from-waste Facilities in the Cement Kiln

Reusing Construction and Demolition Waste to Prepare Alkali-Activated Cement

Utilization of Carbonated Alkaline Solid Wastes in Ordinary Portland Cement-Metakaolin-limestone Ternary Mixture: Underlying the Role of Low Grade-Sustainable Calcium Carbonate Sources

Synthesis of nano-calcium carbonate from waste cement and techno-economic and environmental evaluation

Conjoint Reuse of Ceramic Polishing Waste and Calcium Carbide Slag As Mineral Admixtures: Hydration and Mechanical Properties

A Novel Method for MSWI Fly Ash Resource Based on Calcium Component Regulation and CO2 Mineralization

A Promising Mineralization Method of Recycled Hardened Cement Powder and Its Material Evolution Mechanism in Portland Cement

Research Progress of Low-Carbon Cementitious Materials Based on Synergistic Industrial Wastes

A novel method for MSWI fly ash resource based on calcium component regulation and CO 2 mineralization

Calcined Cutter Soil Mixing Residue-Based Alkali-Activated Cement: Compressive Strengths, Reaction Products, and Sustainability

Upcycling Carbon Dioxide to Improve Mechanical Strength of Portland Cement

Valorization of Deep Soil Mixing Residue in Cement-Based Materials

Carbon Capture and Utilization by mineralization of cement pastes derived from recycled concrete

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Reusing Ceramic Waste as a Fine Aggregate and Supplemental Cementitious Material in the Manufacture of Sustainable Concrete

Effect of Wet Grinding Carbonation of Sintering Red Mud on the Performance of Carbon Sequestered Mortar