Mechanism Underlying Early Hydration Kinetics of Carbonated Recycled Concrete Fines-Ordinary Portland Cement (CRCF-OPC) Paste

Ligang Peng,Yi Jiang,Jiaxing Ban,Yuanyuan Shen,Zihan Ma,Yuxi Zhao,Peiliang Shen,Chi-Sun Poon

DOI: https://doi.org/10.1016/j.cemconcomp.2023.105275

IF: 9.93

2023-01-01

Cement and Concrete Composites

Abstract:Aiming to promote applications of carbonated recycled concrete fines (CRCF) as a low-carbon alternative to ordinary Portland cement (OPC), this study explored the effect of CRCF on the early hydration kinetics of OPC paste. The results show that CRCF is not only a highly active pozzolanic material but also an effective accelerator affecting the early hydration kinetics of OPC paste, thereby leading to an increased early compressive strength and a comparable 28-d compressive strength, even at a replacement ratio of 20%. Although the rheological properties and workability are negatively affected due to the high surface area and fine particle size of CRCF, the amorphous silica and silica-alumina gels and calcite present in CRCF facilitate initial ions dissolution and provide additional active nucleation sites for hydrates. As a result, the microstructure is densified due to the formation of additional C–S–H gels with high Si/Ca and Al/Ca ratios and carboaluminate phases, along with the inert filler effect of unreacted calcite particles. The incorporation of 20% CRCF to replace OPC can achieve a CO2 emissions reduction up to 25%. These indicate that the CRCF has a promising application scenario in transforming wasted concrete into high-value industrial products by CO2 activation.