Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Revealing internal corrosion of GH4169 with stress coupled solid NaCl deposited in a humid environment of 600 °C

Exploration on the Stress-induced Internal Corrosion of NaCl-Deposited GH4169 Under Humid Intermediate Temperature Environments

Corrosion Behavior of Pre-oxidized GH4169 Alloy with Solid NaCl Deposited in a Wet Oxygen Flow at 600 °C

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Influence of temperature on hot corrosion behavior of GH4169 superalloy subjected to Na 2 SO 4 -NaCl salts attack

Corrosion Behavior of the GH3535 and C276 Alloys at the Liquid/Gas LiCl–KCl Salt Interface at 550 °C

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Influence of Hot Corrosion on Precipitation of Phase and Tensile Properties of GH4169 Superalloy

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: Initial corrosion with tensile stress coupling

Stress-assisted corrosion behaviour of Hastelloy N in FLiNaK molten salt environment

Corrosion mechanism of K411 superalloy in sulfur-containing environment: sulfidation promoting internal nitridation

AgCl-induced hot salt stress corrosion cracking in a titanium alloy

Corrosion behavior of carburized 316 stainless steel in molten chloride salts

High-temperature corrosion of a Si3N4/W composite exposed to molten MgCl2-NaCl-KCl salts

The characterization of corrosion layers of GH3535 and Inconel 625 alloys in molten KNO3-NaNO3 salts at 500 °C

Corrosion behavior and mechanism of GH3535 alloy in NaOH, HF and H2O2 solution

Nucleation of stress corrosion cracking in aluminum alloy 6061 in sodium chloride solution: Mechanical and microstructural aspects

Quantitatively evaluating the contribution of intergranular carbides, Cr-depleted zone, and grain boundary to intergranular stress corrosion cracking of Alloy 600 in a simulated boiling water reactors environment with high oxygen concentrations

Research on Hot Corrosion Behavior of DZ40M and K452 Superalloys in NaCl Molten Salt

Hot Corrosion Mechanism of Nickel-Based Single Crystal Superalloy IC21 under Flowing Atmosphere