Abstract:In recent years, weight reduction of automobile bodies has been effective in reducing carbon dioxide emissions. For this reason, the replacement of steel, which has a large specific gravity, with aluminum alloys and carbon fiber reinforced plastics is being promoted for the right materials in the right places. In this case, an appropriate dissimilar material joining method is needed in terms of ease of assembly, joining performance, and cost. Friction stir welding (FSW) has emerged as a promising joining method for a variety of engineering applications. FSW is a solid-phase joining technique that has been shown to have significant advantages over conventional welding in terms of the strength and quality of the joints produced. However, during joining of metallic materials by FSW, microstructural changes may occur that affect their corrosion degradation. In this study, the corrosion behavior of A6061 jointed with high-strength steel (SPCC980) by FSW in aqueous NaCl solution and the effect of Al alloy microstructural changes on it were investigated. In this study, FSW was performed on A6061 and SPCC980 steel plates, and galvanic corrosion behavior was investigated by immersion tests and surface observations, as well as electrochemical measurements of Al alloys. Immersion tests were performed in 1 M NaCl solution. Micro electrochemical polarization tests of A6061 were also performed to investigate the corrosion behavior. In the immersion test of the galvanic couple of A6061 and SPCC980 steel plates in NaCl solution, galvanic corrosion occurred with the Al alloy as the anode and the steel plate as the cathode, and hydrogen evolution was observed mainly from the BM site on A6061 in the initial stage of immersion. This is due to the hydrogen evolution reaction occurring inside the pitting corrosion of the A6061. The pits was formed near Fe-rich inclusions in the BM site. In the HAZ site, corrosion propagated from Fe-rich inclusions along grain boundaries, but no pitting corrosion was formed. In the NZ site, minor localized corrosion was developed. These results indicate that the susceptibility to localized corrosion and its morphology differ in each site on the A6061. The difference in localized corrosion susceptibility on the A6061 was considered to be caused by the difference in the distribution of Fe-rich inclusions. However, the fact that the size and number of Fe-rich inclusions in each site did not differ suggests that the difference in anodic dissolution activity near Fe-rich inclusions affects pitting corrosion susceptibility in each site. A6061 alloy is a precipitation-strengthened Al alloy reinforced by β'' phase, which is a metastable phase of Mg 2 Si, and dense precipitation of β'' phase was observed in the BM site. Therefore, the reason for the higher localized corrosion susceptibility of BM is related to the precipitation of the β'' phase. This paper is based on results obtained from a project, JPNP14014, commissioned by the New Energy and Industrial Technology Development Organization (NEDO).

Nucleation of stress corrosion cracking in aluminum alloy 6061 in sodium chloride solution: Mechanical and microstructural aspects

Investigation on corrosion fatigue properties of TA15 alloy in 3.5%NaCl salt spray

Stress Corrosion of an Aluminum Alloy in Sodium Chloride Solution under Different Temperatures and Stresses

Short Surface Crack Growth of High-Strength Aluminum Alloy in Corrosion Fatigue.

Mechanism of corrosion fatigue fracture of friction stir welding joints of 7075 aluminium alloy in 3.5% NaCl solution

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile

Nanoscale perspective on the stress-corrosion cracking behavior of a peak-aged 7XXX-Al alloy

Three-dimensional Quantitative in Situ Study of Crack Initiation and Propagation in AA 6061 Aluminum Alloy Sheets Via Synchrotron Laminography and Finite-Element Simulations

Revealing internal corrosion of GH4169 with stress coupled solid NaCl deposited in a humid environment of 600 °C

The influence Cl- on stress corrosion of 7 xxx series aluminium alloys studied by experimental and simulation technology

Stress corrosion crack initiation in Alloy 690 in high temperature water

Environment-Assisted Fatigue Crack Growth Along A1-6061/Epoxy Interface

Study on the initiation stage of stress corrosion of an aluminum alloy using the subjective speckle technique

Corrosion fatigue crack propagation of 7XXX series aluminum alloys from key components of high-speed train

Corrosion Behavior of Al Alloy A6061 Jointed with High-Tensile Strength Steel By Friction Stir Welding in NaCl Solution

Nanoscale corrosion investigation of surface nanocrystallized 7150 Al alloy in 3.5 wt% NaCl solution by using FIB-TEM techniques

The mechanisms of hot salt stress corrosion cracking in titanium alloy Ti-6Al-2Sn-4Zr-6Mo

Fatigue crack nucleation and microstructurally small crack growth mechanisms in high strength aluminum alloys

Stress-assisted corrosion behaviour of Hastelloy N in FLiNaK molten salt environment

Environment-induced Fatigue Cracking Behavior of Aluminum Alloys and Modification Methods

Numerical and experimental study of the hot cracking phenomena in 6061/7075 dissimilar aluminum alloy resistance spot welding