Large-area anode-supported protonic ceramic fuel cells combining with multilayer-tape casting and hot-pressing lamination technology

Zuzhi Huang,Yang Yang,Haipeng Lv,Caixia Shi,Tian Li,Yihan Ling,Ting Chen,Shaorong Wang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.09.057
IF: 5.7
2022-10-04
Journal of the European Ceramic Society
Abstract:Anode-supported protonic ceramic fuel cells (PCFCs) have many advantages such as the excellent performance and durability at lower temperatures. However, the fabrication of large-area PCFCs is still a big challenge. In this work, the anode supported 10 × 10 cm 2 PCFCs with BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ (BZCYYb) electrolyte are fabricated by an optimized sintering process combining with multilayer-tape casting and hot-pressing lamination technology. Through optimizing the sintering shrinkage and thermal expansion behavior, anode supported large-area PCFCs with dense BZCYYb electrolyte are obtained with optimal sintering process. The maximum power density of the cell using H 2 as fuel reaches 400 mW/cm 2 at 700 °C. The cell also shows a good thermal cycling performance and durability in 425 h test. Preliminary experimental results indicate that the fabrication technology with multilayer-tape casting and hot-pressing lamination is successful for large-area PCFCs, which can improve the cell fabrication efficiency and provide positive reference for large-area PCFCs.
materials science, ceramics
What problem does this paper attempt to address?