Isotropic and improved tensile properties of Ti-6Al-4V achieved by in-situ rolling in direct energy deposition

Xinni Tian,Yuman Zhu,Chao Voon Samuel Lim,James Williams,Rod Boyer,Xinhua Wu,Kai Zhang,Aijun Huang

DOI: https://doi.org/10.1016/j.addma.2021.102151

IF: 11

2021-10-01

Additive Manufacturing

Abstract:<p>The longstanding issue in additive manufacturing (AM) of titanium alloys is the large, columnar grains created by the intrinsic directional heat flow along the build direction. These long grains lead to strongly anisotropic mechanical properties that impede the qualification and applications of the final products. In this work, a novel in-situ rolling technique coupled with the direct energy deposition (DED) was developed to fabricate a Ti-6Al-4V alloy part. Through this hybrid technique, excellent isotropic tensile properties were achieved for thin-wall components. The strength and uniform elongation along two mutually perpendicular directions exhibited good consistency with negligible property scatter. Further studies revealed that the isotropic tensile properties were associated with the formation of nearly equiaxed prior-β grains uniformly distributed throughout the whole sample. Meanwhile, the internal α grains exhibited around 2.5 times weaker textures in the rolled compared to the unrolled DED samples. Moreover, strength increases were observed for samples produced by in-situ rolling in DED. This enhanced tensile strength was attributed to the heavily refined prior-β grains compared to those in the unrolled sample. In addition, an interface phase with a face-centred cubic structure (FCC, <em>a</em> = 0.43 nm) was observed between the α and β phases in both unrolled and in-situ rolled samples. The processing method in this work is applicable to other metallic materials to remove the columnar grain structures and provide improved mechanical performance.</p>

engineering, manufacturing,materials science, multidisciplinary