Enhanced Performance of Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 Solid Electrolyte by the Regulation of Grain and Grain Boundary Phases

Zeya Huang,Linhui Chen,Bing Huang,Biyi Xu,Gang Shao,Hailong Wang,Yutao Li,Chang-An Wang
DOI: https://doi.org/10.1021/acsami.0c18674
2020-12-01
Abstract:The application of Li-ion conducting garnet electrolytes is challenged by their large interfacial resistance with the metallic lithium anode and the relative small critical current density at which the lithium dendrites short-circuit the battery. Both of these challenges are closely related to the morphology and the structure of the garnet membranes. Here, we prepared four polycrystalline garnet Li<sub>6.4</sub>La<sub>3</sub>Zr<sub>1.4</sub>Ta<sub>0.6</sub>O<sub>12</sub> (LLZTO) pellets with different particle sizes (nano/micro) and grain boundary additive (with/without Al<sub>2</sub>O<sub>3</sub>) to investigate the influence of grain size, the composition of the grain boundary, and the mechanical strength of the pellet on the total Li-ion conduction of the pellet, Li/garnet interfacial transfer, and lithium dendrite growth in all-solid-state Li-metal cells. The results showed that the garnet pellets prepared with nanoparticles and LiAlO<sub>2</sub>-related grain boundary phase had decreased total Li-ion conductivity because of the increased resistance of the grain boundary; however, these pellets showed higher mechanical strength and improved capability to suppress lithium dendrite growth at high current densities. By controlling the grain size and optimizing the grain boundary with Al<sub>2</sub>O<sub>3</sub> sintering additive, the hot-pressing sintered LLZTO solid electrolytes can reach up to 1.01 × 10<sup>–3</sup> S cm<sup>–1</sup> in Li<sup>+</sup> conductivity and 0.29 eV in activation energy. LLZTO with nanosized grain and LiAlO<sub>2</sub>-modified grain boundary showed the highest critical current density, which is 0.6 mA cm<sup>–2</sup> at room temperature and 1.7 mA cm<sup>–2</sup> at 60 °C. This study offers a useful guideline for preparing a high-performance LLZTO solid electrolyte.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18674?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18674</a>.Feature sizes of LLZTO powders prepared by hand milling and sand milling (Table S1); XRD patterns of hot-pressing sintered samples (Figure S1); element distribution on the polished surface of the sintered samples containing Al<sub>2</sub>O<sub>3</sub> and without Al<sub>2</sub>O<sub>3</sub> by EDX scan (Figure S2); equivalent circuit model for EIS fitting (Figure S3); and LLZTO specimens fractured by three-point bending test, gold sprayed on the surface of the micro-solid electrolyte, an optical photo of the micro-lithium symmetrical battery, and a micro-test fixture designed to test the micro-battery (Figure S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18674/suppl_file/am0c18674_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?