Microstructural engineering for Ta-doped Li-garnet solid electrolyte toward enhancing performance

Fugang Lu,Jiujie Xu,Zhanguo Liu,Tiesong Lin,Xin Yue,Xiaoming Duan,Jincheng Lin,Xinyue Li,Xinfei Zhang,Panpan Lin,Ce Wang,Peng He

DOI: https://doi.org/10.1016/j.ensm.2023.103101

IF: 20.4

2023-12-02

Energy Storage Materials

Abstract:Solid-state lithium batteries (SSLBs) based on Li-garnet solid electrolytes have received tremendous attention owning to their strong safety and high energy density. However, poor ionic conductivity at room temperature and low relative density of Li-garnet solid electrolytes hinder their widespread applications. Herein, microstructural engineering enabled by further Yb-doping strategy is adopted to enhance the performance of Li-garnet solid electrolyte Li 6.5 La 3 Zr 1.5 Ta 0.5 O 12 (LLZTO). The introduction of Yb exerts dual regulation of intragrain and grain boundary, enlarging the bottleneck size for Li + migration and suppressing abnormal grain growth (AGG), which enhance ion conductivity and fabricate homogeneous dense electrolyte. First principles calculation demonstrates Yb into electrolyte can reduce Gibbs free energy change ( ΔG ) of electrolyte reaction, making sintering process easier to complete. A dense microstructure is obtained when 0.1 Yb is doped LLZTO, and the maximum ion conductivity achieves 7.67 × 10 −4 S·cm −1 with relative density of 96.2%. The critical current density (CCD) of Li symmetric cell composed of 0.1Yb-LLZTO reaches 1.30 mA cm −2 and provides stable cycling performance for 4000 h at 0.1 mA cm −2 . Additionally, SSLB matched with 0.1Yb-LLZTO and LiFePO 4 delivers a remarkable cycling performance with a discharge capacity of 125.4 mAh g −1 and capacity retention of 83.2% after 300 cycles (0.5 C). The findings of this study provide important implications for understanding microstructural engineering in electrolyte preparation and developing high-performance Li-garnet-based SSLBs.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology