Abstract:Thin-gauge non-oriented silicon steel with high strength was successfully processed using strip casting. Texture evolution and strengthening mechanism via nanoscale Cu-rich precipitates were studied to fundamentally understand the balanced combination of magnetic properties and mechanical properties. Coarse equiaxed grains with average size of ∼190 μm and relatively random texture were formed in the as-cast strip, which contributed to the inhomogeneous deformation, resulting in high density of shear bands. Exact Cube was retained from the initial Cube texture and new Goss was formed during the heavy rolling process in the 0.20 mm cold rolled sheet, which promoted relatively strong Cube and Goss texture after recrystallization annealing. The 0.20 mm annealed sheet exhibited high magnetic induction of 1.709 T, which corresponds to the high texture factor of 0.5. The total iron losses were significantly reduced with decrease in thickness, and the P1.5/50, P1.0/400, and P1.0/1000 in 0.20 mm sheet were as low as 2.63, 15.17 and 55.63 W/kg, respectively, which showed a good match between magnetic induction and iron loss. During the aging process, both the magnetic induction and total iron loss exhibited relatively good stability. With increase in aging time, the yield strength first rapidly increased and then slightly decreased. In 0.20 mm sheet, peak yield strength of ∼630 MPa was obtained on aging at 550 °C for 90–120 min. The key mechanism of precipitation strengthening was attributed to the difference in modulus and coherency strain associated with high density of nanoscale precipitates of ∼5 nm. The study revealed that the nanoscale Cu-rich precipitates can be adopted as effective approach to increase the yield strength over ∼100 MPa without deteriorating iron loss in thin-gauge non-oriented silicon steel by strip casting, which guaranteed the balance of magnetic properties and mechanical properties to meet the requirements of high-speed motor.

Development of non-oriented silicon steel sheet with very low core loss

Application and Development of High Magnetic Flux Density Low Iron Loss Non-oriented Silicon Steel

Development of thin-gauge low iron loss non-oriented silicon steel

Study on microstructure and texture of a new-type low Si high Mn non-oriented silicon steel 50W250

Fabrication of high-performance low silicon non-oriented electrical steels by a new method: Low-finishing-temperature hot rolling combined with batch annealing

Decreasing the Core Loss of Grain-Oriented Silicon Steel by Laser Processing

Thick-Gauge Ultra-High-Strength High-Silicon Non-Oriented Silicon Steel with Balanced Mechanical and Magnetic Properties Controlled by Partial Recrystallization Annealing

Roles of Silicon Content and Normalization Temperature on Cold Workability and Recrystallization of High-Grade Non-Oriented Silicon Steel

Influence of Annealing Process on Microstructures,Mechanical and Magnetic Properties of Nb-Containing High-Strength Non-Oriented Silicon Steel

Method for producing high magnetic induction orientation silicon steel with excellent magnetic performance and good bottom layer

Residual deformation analysis of grain-oriented silicon steel sheets with lowered core loss using laser processing

Ultrathin-gauge high silicon non-oriented electrical steel with high permeability and low core loss fabricated by optimized two-stage cold rolling method

Evolution of {0kl} 〈1 0 0〉 texture and microstructure in preparation of ultra-thin grain-oriented silicon steel

Ultra-thin grain-oriented silicon steel sheet fabricated by a novel way: Twin-roll strip casting and two-stage cold rolling

Thin-gauge non-oriented silicon steel with balanced magnetic and mechanical properties processed by strip casting

Microstructure and texture evolution of ultra-thin grain-oriented silicon steel sheet fabricated using strip casting and three-stage cold rolling method

Twin Roll Casting and Secondary Cooling of 6.0 wt.% Silicon Steel

Microstructure and texture evolution of thin-gauge non-oriented silicon steel with high permeability produced by twin-roll strip casting

Novel Process for the Formation of Goss Grains by Concentrated Shear Strain on Surface in Inhibitor-Free Silicon Steel

Microstructural evolution and magnetic properties in strip cast non-oriented silicon steel produced by warm rolling