On the Effect of Exposure Time on Al-Si10-Mg Powder Processed by Selective Laser Melting

Paola Leo,Gilda Renna,Neetesh Soni,Fabio De Pascalis,Teresa Primo,Antonio Del Prete

DOI: https://doi.org/10.3390/met14010076

IF: 2.695

2024-01-09

Metals

Abstract:In this study, the effect of increasing exposure time on the microstructures, porosity, mechanical properties and corrosion behavior of selective laser melted sample Al-Si10-Mg powder was investigated. The samples were processed at the same power (375 W) and scan speed (2000 mm/s), but with increasing exposure time. Exposure time equal to 40, 50 and 60 μs was applied. The features of the analyzed samples show that with increasing exposure time, greater efficiency of the heat input was obtained, with a larger size of the melt pool and Si particles and lower porosity. Specifically, at the highest exposure time the melt pool showed an increase of 19% in width and 48% in depth, while the volume percentage of the voids decreased by 50% with respect to the lowest exposure time. Moreover, with the coarser microstructure being associated with a lower level of voids, the average hardness is similar for the analyzed samples. Corrosion resistance was evaluated, being one of the most important properties that may affect the service performance of Al-Si10-Mg alloy in the aerospace, marine and automotive industries. The potentiodynamic curves of the samples show that the voids occurrence is more significant with respect to the scale of the microstructure on corrosion behavior, with the sample processed at the highest exposure time being the more resistant to corrosion. The experimental techniques used in the present study were Optical Microscope (OM), Scanning Electron Microscope (SEM), hardness and X-Ray Computed Tomography.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem this paper attempts to address is: studying the impact of exposure time on the microstructure, porosity, mechanical properties, and corrosion behavior of Al-Si10-Mg powder material during the Selective Laser Melting (SLM) process.

Specifically, the authors investigate the effects of different exposure times (40 μs, 50 μs, and 60 μs) under the same laser power (375 W) and scanning speed (2000 mm/s) on the following aspects:

1. **Microstructure**: With the increase in exposure time, the thermal input efficiency improves, the melt pool size increases, Si particle size enlarges, and porosity decreases.
2. **Porosity**: The sample with the highest exposure time shows a 50% reduction in pore volume.
3. **Mechanical Properties**: Despite the coarsening of the microstructure, the hardness remains similar.
4. **Corrosion Resistance**: Electrochemical tests reveal that the presence of pores significantly affects corrosion behavior, with the sample treated at the highest exposure time exhibiting the strongest corrosion resistance.

Through these studies, the authors aim to reveal the impact of exposure time on the properties of Al-Si10-Mg alloy in the SLM process, thereby providing a scientific basis for optimizing process parameters.