Effect of holding time on microstructure and mechanical properties of dissimilar γ'‐strengthened superalloys TLP joint
Yikai Yang,Jian Ding,Yujiang Wang,Yingli Zhao,Haomin Feng,Sufang Li,Rui Guo,Ying Tang,Wen Chen,Ri Li,Linjun Chen,Ji Dong,Xingchuan Xia
DOI: https://doi.org/10.1002/adem.202300460
IF: 3.6
2023-05-27
Advanced Engineering Materials
Abstract:To achieve efficient connectivity of dissimilar γ'‐strengthened superalloy, transient liquid‐phase (TLP) diffusion bonding of 718Plus and Ni3Al‐based superalloys was carried out using BNi‐2 interlayer at a constant temperature of 1100°C with holding times of 3, 15, 30 and 60 min. The results showed that when the holding time was insufficient, isothermal solidification transformed into athermal solidification. Due to the enrichment of B and Cr elements in liquid phase, ternary eutectic consisting of γ, Ni3B and CrB was formed at the joint center. Ternary eutectic with higher hardness(∽600 Hv) was poorly bonded to the matrix, which can easily become crack initiation location and significantly deteriorated the tensile properties. In addition, microhardness of the joint became more uniform and tensile strength gradually increased due to the reduction of eutectic with holding time increasing. Isothermal solidification completed and a joint without eutectic structure was formed at 1100°C for 60 min. Diffusion of Al atoms led to the formation of γ' with gradient size and tensile strength was comparable to that of base metal which was about 690.93 MPa. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary