Abstract:The effect of different parameters on the microstructure and mechanical properties of dissimilar joints between WC-10Co and 316L stainless steel using the transient liquid phase process was investigated. Temperatures of 1100 and 1150 °C, along with holding times of 1, 15, 30, and 45 min, were utilized to create the joints, using a BNi-2 interlayer with 50 μm thickness. The microstructure of the joints was examined using a scanning electron microscope equipped with energy-dispersive x-ray spectroscopy. Additionally, x-ray diffraction analysis was employed to identify the phases in the bonding area. Microhardness and shear–tensile strength tests were conducted to study the mechanical properties of the joints. The results showed that the bonding area encompasses several zones, including the solidification and diffusion-affected zones. The solidification zone was formed based on the isothermal solidification mechanism, resulting in the production of a nickel-based solid solution within this zone. Also, secondary phase precipitates and the η-phase formed within the diffusion-affected zones. The volume and distribution of these phases depended on the bonding parameters. The results of XRD analysis confirmed that there are phases such as nickel-based solid solution, WC and η-phase in the bonding area. The highest tensile–shear strength was observed in the bonded sample processed at 1100 °C with a holding time of 15 min, attributed to the optimal quantity and thickness of the η-phase within the DAZ of the WC-Co base material.

The Effect of Bonding Time and Temperature on Microstructure and Mechanical Properties of SS316L/WC-Co Dissimilar Joint Produced by Transient Liquid Phase Bonding