Abstract:Earthquake-induced fractures in steel structures are characterised by high-strain low-cycle conditions. In order to investigate the ultra-low cyclic fatigue fracture of steel welded joints under earthquakes, two most commonly used structural steels (Q235B and Q345B) and the corresponding welds were studied by experiments and numerical analysis in this paper. Specimens were extracted from the base material, the weld metal and the heat affected zone to investigate the behaviour in different parts of the welded joint. Eighteen smooth round bars were tested under large strain amplitudes, the hysteretic properties, damage degradation characteristics and failure process were analyzed. Constitutive model named Chaboche model was calibrated to describe the cyclic hardening behaviour of these materials. Seventy-two notched round bars with three different notch sizes and two loading protocols were tested to study the fracture behaviour of different materials at different stress triaxialities and different strain amplitudes. Two micromechanical fracture models: cyclic void growth model and degraded significant plastic strain model were calibrated based on the test results. The micromechanical models and Chaboche model were incorporated into numerical simulations by software ABAQUS with subroutine VUMAT to predict the materials fracture. The results show that the failure process under cyclic loads is opposite to that of monotone loads. The dissipation capacity of Q345B is superior to that of Q235B. The fracture resistance deteriorate more in the weld zone under the same loading conditions. The validated models can be used to effectively and accurately evaluate the fracture in steel welded connections under ULCF conditions.

Fracture prediction of circular steel tubular X-joints using a Lode parameter enhanced cyclic void growth model

Improvement Of Cyclic Void Growth Model For Ultra-Low Cycle Fatigue Prediction Of Steel Bridge Piers

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

A Novel Machine-Learning Based Framework for Calibrating Micromechanical Fracture Model of Ultra-Low Cycle Fatigue in Steel Structures

Study on Ultra‐low Cycle Fatigue Fracture of Thick‐walled Steel Bridge Piers

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Low-Cycle Fatigue Test of Circular Concrete Filled Tubular Columns

Continuous damage model for structural steels and weld metals under ultra-low-cyclic loading

Extremely low cycle fatigue prediction of steel beam-to-column connection by using a micro-mechanics based fracture model

Experimental and numerical investigations on extremely-low-cycle fatigue fracture behavior of steel welded joints

Fracture prediction in transverse fillet welded joints of high strength structural steel

Fracture prediction of Fe-SMA under monotonic and low cycle fatigue loading

A Simple Calibrated Ductile Fracture Model and Its Application in Failure Analysis of Steel Connections

Fracture Prediction of Welded Steel Connections Using Traditional Fracture Mechanics and Calibrated Micromechanics Based Models

Ultra-Low Cyclic Fatigue Fracture of Q235B and Q345B Steels and Their Butt Welded Joints

A cyclic GTN model for ultra-low cycle fatigue analysis of structural steels