Abstract:Digital light processing (DLP) is increasingly widely used to manufacture high-precision complex structural ceramic components quickly and efficiently. However, due to the high absorbance of silicon carbide (SiC) micron fine powder and the high refractive index difference between the powder and the photosensitive resin, it is extremely challenging to DLP print SiC with high precision complex structure. Here, the surface of SiC powder was coated with SiO 2 nano-layer of different thickness by controllable oxidation coating method, thus realizing the photocurable printing of SiC@SiO 2 green bodies with structural precision up to 80 μm. Through the two-step reaction method of carbothermal reduction combined with gas-phase siliconizing (GSI), not only the SiO 2 coated layer was effectively removed, but also the reaction-bonded silicon carbide (RB-SiC) ceramics with 80–300 μm periodic structure was successfully realized. Ultimately, the comprehensive performance of the RB-SiC samples is effectively improved by chemical vapor infiltration of silicon carbide (CVI-SiC). It is noteworthy that the maximum elastic modulus and hardness of the ultima SiC specimens (RB-SiC@CVI-SiC) are as high as 394.599 GPa and 50.241 GPa, respectively. Shockingly, the nanomechanical properties of postgenetic RB-SiC bound to initial α-SiC on the cross-section of ultima specimens were much higher than those of CVI-SiC on the surface. This study fills the gap that liquid-phase siliconizing (LSI) or pyrolysis process could not achieve high-performance SiC ceramics with micron-level periodic structure.

Surface modification of superfine SiC powders by ternary modifiers-KH560/sodium humate/SDS and its mechanism

Influence of Silane Coupling Agent and Anionic Dispersant on the Dispersion Effect of Silicon Carbide Particles

Composite modification of fine SiC powder by 3-aminopropyl triethoxysilane and sodium polystyrene sulfonate and its slip casting study

Surface Modification of Halloysite/Sericite

DISPERSIBILITY MECHANISM AND SPRAY DRYING OF SiC AQUEOUS SLURRY

Influence of surface oxide layer of SiC powder on the rheological properties of its slurry

Formation mechanism of stereolithography of Si3N4 slurry using silane coupling agent as modifier and dispersant

The effects of surfactants on CIM of Si3N4

Surface modification of Si3N4 ceramic powders by emulsion polymerization

Surface Modification to Produce Hydrophobic Nano-Silica Particles Using Sodium Dodecyl Sulfate As a Modifier

Rheological properties and spray-drying behaviors of nano-SiC based aqueous slurry

Controllable reduction of absorbance and two-step reaction for 3D-printed SiC ceramics with micron-level periodic structure

Modification of Nanosilica Particles with Hydrophobic Modifier Bis[3-(Triethoxysilyl)propyl]tetrasulfide by Using Micro-Injection in Aqueous Solutions

Si 3 N 4 slurry with high solid phase, low viscosity prepared via surface-oxidation and silane coupling agent modification hybrid method

Preparation of CIM Feedstock of Al2O3-SiC Nanocomposite

Characterization of mechanochemical modification in SiC powder

Surface Modification of Ceramic Powders by Titanate Coupling Agent for Injection Molding Using Partially Water Soluble Binder System

Surface Modification and Water Debinding in Zirconia Powder Injection Molding

Study on the Rheology of Acetic Acid Modified SiC Powder and Pastes Reinforced by Solvothermal Method

Aqueous Processing, Hot-Pressing and Mechanical Properties of Silicon Carbide with Al2O3 and Y2O3

Surface Modification Of Nano-Sic Powders By Coating With Heterogeneous Nucleation Process