Influence of Calcareous Deposits on Hydrogen Embrittlement Susceptibility of Q460 Steel

Xilin Xiong,Haichun Yang,Tongqian Chen,Na Zhang,Tong Niu

DOI: https://doi.org/10.3390/ma17051110

IF: 3.4

2024-02-29

Materials

Abstract:Cathodic protection is widely used to protect structural steel from corrosion in marine environments. However, an inappropriate cathodic potential may lead to hydrogen embrittlement (HE). Therefore, this study investigates the relationship between cathodic protection potential, structure and composition of calcareous deposits, and hydrogen embrittlement susceptibility of Q460 steel. The slow strain rate test results and fracture analysis reveal that Q460 steel had the smallest HE susceptibility when covered with the calcareous deposits formed under −1.1 VSCE. The deposits have a relatively thin calcium-rich inner layer and a condensed magnesium-rich outer layer, which can significantly inhibit hydrogen entry. A sustained deposition reaction during slow strain rate testing (SSRT) in artificial seawater can also decrease the HE susceptibility of Q460 steel.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily investigates the impact of calcareous deposits on the hydrogen embrittlement susceptibility of Q460 steel. The study evaluates how calcareous deposits formed under different cathodic protection potentials affect the hydrogen embrittlement behavior of Q460 steel through slow strain rate tests (SSRT).

Specifically, the paper addresses the following key issues:
1. **Effect of Cathodic Protection Potential**: The study examines the impact of different cathodic protection potentials (ranging from -1.0 to -1.3 V relative to the saturated calomel electrode [SCE]) on the formation of calcareous deposits and the hydrogen embrittlement susceptibility of Q460 steel.
2. **Analysis of Calcareous Deposit Structure and Composition**: Experimental observations revealed that calcareous deposits formed under different cathodic protection potentials exhibit distinct structural and compositional characteristics. In particular, deposits formed at -1.1 V SCE have a thin calcium-rich inner layer and a dense magnesium-rich outer layer, which helps inhibit hydrogen ingress.
3. **Evaluation of Hydrogen Embrittlement Susceptibility**: The study assesses the impact of calcareous deposits on the hydrogen embrittlement susceptibility of Q460 steel under different conditions using SSRT. The results show that calcareous deposits formed at -1.1 V SCE significantly reduce the hydrogen embrittlement susceptibility of Q460 steel.
4. **Role of Continuous Deposition Reaction**: During SSRT in artificial seawater, calcareous deposits continue to form, and this dynamic process further reduces the hydrogen embrittlement susceptibility of Q460 steel.

In summary, this study aims to reveal how the structure and composition of calcareous deposits, along with cathodic protection potential, collectively influence the hydrogen embrittlement phenomenon in Q460 steel. It provides important insights into how these factors can be regulated to reduce the risk of hydrogen embrittlement in materials.