Abstract:The hydrogen concentration in steel is directly related to the hydrogen embrittlement (HE) sensitivity of the steel. This study combined electrochemical hydrogen charging, the slow strain rate test (SSRT), and hydrogen permeation experiments to investigate the variation in the hydrogen concentration in pipeline steel with the electrochemical hydrogen-charging time. The influence of the hydrogen concentration in steel on the mechanical properties of X80 pipeline steel was obtained, and ultimately, a quantitative relationship between the hydrogen concentration in steel and the hydrogen embrittlement sensitivity was established. The results show that the hydrogen concentration in the steel gradually increased with the time of hydrogen charging, and the quantitative relationship formula can be given as CH = 5.35 − 4.2 exp (−0.26t); the HE index of X80 steel increased with the hydrogen concentration. Additionally, once the hydrogen concentration in steel reaches 5.08 × 10−6 mol/cm3, even the slightest alteration in the hydrogen content will precipitate a dramatic decrease in plasticity. The quantitative relationship formula between the hydrogen concentration and the HE index (FH) in X80 steel can be given as FH = 0.029 exp (1.5CH) – 0.029. When the hydrogen concentration in steel is at a maximum, the FH of X80 steel reaches 88.6%. This study provides a reference for analyzing the quantitative relationship between the hydrogen concentration and the HE index in steel after electrochemical hydrogen charging.

What problem does this paper attempt to address?

The paper attempts to address the quantitative relationship between hydrogen concentration and hydrogen embrittlement sensitivity of X80 pipeline steel. Specifically, the study aims to explore the changes in hydrogen concentration in X80 pipeline steel under different electrochemical hydrogen charging times through electrochemical hydrogen charging, slow strain rate test (SSRT), and hydrogen permeation experiments, and to establish a quantitative relationship between hydrogen concentration and hydrogen embrittlement sensitivity. ### Main Research Content: 1. **Changes in Hydrogen Concentration**: - The changes in hydrogen concentration in X80 pipeline steel under different electrochemical hydrogen charging times were studied. - A quantitative relationship formula for hydrogen concentration with hydrogen charging time was established: \[ C_H = 5.35 - 4.2 \exp(-0.26t) \] 2. **Impact on Mechanical Properties**: - The impact of hydrogen concentration on the mechanical properties of X80 pipeline steel was explored. - It was found that with the increase in hydrogen concentration, the plasticity of X80 pipeline steel significantly decreased, while the hydrogen embrittlement index (FH) gradually increased. 3. **Quantitative Relationship of Hydrogen Embrittlement Sensitivity**: - A quantitative relationship formula between hydrogen concentration and hydrogen embrittlement index was established: \[ F_H = 0.029 \exp(1.5 C_H) - 0.029 \] - When the hydrogen concentration reaches the maximum value \( 5.35 \times 10^{-6} \text{mol/cm}^3 \), the hydrogen embrittlement index reaches a maximum value of 88.6%. ### Research Methods: 1. **Materials and Sample Preparation**: - Commercial X80 pipeline steel plates were used to prepare hydrogen permeation, hydrogen concentration testing, and SSRT samples. 2. **Hydrogen Permeation Experiment**: - Electrochemical hydrogen permeation experiments were conducted using a Devanathan–Stachurski double-cell apparatus to determine the time required for hydrogen saturation. 3. **Quantitative Testing of Hydrogen Concentration**: - Electrochemical methods were used to measure the hydrogen concentration at different hydrogen charging times. 4. **Slow Strain Rate Test (SSRT)**: - SSRT was used to evaluate hydrogen embrittlement sensitivity, obtain stress-strain curves, and observe the fracture morphology of the samples. ### Conclusion: - This study established a quantitative relationship between hydrogen concentration and hydrogen embrittlement sensitivity of X80 pipeline steel, providing a reference for analyzing the relationship between hydrogen concentration and hydrogen embrittlement sensitivity in steel after hydrogen charging.

Quantitative Study on Hydrogen Concentration–Hydrogen Embrittlement Sensitivity of X80 Pipeline Steel Based on Hydrogen Permeation Kinetics