Abstract:Antimony chalcogenides are widely studied as a light-absorbing material due to their merits of low toxicity, efficient cost, and excellent photovoltaic properties. However, the band gaps of antimony selenide (approximately 1.1 eV) and antimony sulfide (approximately 1.7 eV) both deviate from the optimal detailed balance band gap (∼1.3 eV) for terrestrial single-junction solar cells. Notably, the band gap of Sb2(S, Se)3 can be tunable in the range from 1.1 to 1.7 eV, which can cover the detailed balance band gap. In this work, the vapor transport deposition method with two independent evaporation sources is used to deposit Sb2(S, Se)3 thin films. By carefully optimizing the evaporation temperature and the start evaporation time of the Sb2Se3 and Sb2S3 sources, a suitable band gap of 1.33 eV is obtained. Finally, on the basis of the optimal Sb2(S, Se)3 films, Sb2(S, Se)3 solar cells without a hole transport layer achieved an efficiency of 7.03%.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c10758.Saturated vapor pressure curves of Sb2Se3 and Sb2S3; temperature–time curves of Sb2Se3 and Sb2S3 sources; top-view SEM images at different Sb2Se3 and Sb2S3 source temperatures; XRD diffraction pattern under different Sb2Se3 and Sb2S3 source temperatures; transmission spectroscopy at different Sb2Se3 and Sb2S3 source temperatures; schematic diagram of thin-film light absorption; heating process of the uniform Sb2(S, Se)3 films and band gaps of Sb2(S, Se)3 films; 1/C2–V curves of the devices; band gaps of the devices obtained from EQE data; J–V curves under different light intensities; atomic and ionic radii; material parameters for SCAPS simulations; CdS trap state parameters for SCAPS simulations; and Sb2(S, Se)3 trap state parameters (PDF)This article has not yet been cited by other publications.

Band Gap Adjustable Antimony Selenosulfide Indoor Photovoltaics with 20% Efficiency

Over 7% Efficiency of Sb2(S,Se)3 Solar Cells Via V‐Shaped Bandgap Engineering

Additive Engineering for Sb_2S_3 Indoor Photovoltaics with Efficiency Exceeding 17

Additive engineering for Sb2S3 indoor photovoltaics with efficiency exceeding 17

Additive engineering for Sb 2 S 3 indoor photovoltaics with efficiency exceeding 17%

HTL-Free Sb 2 (S, Se) 3 Solar Cells with an Optimal Detailed Balance Band Gap

Efficient Sb2S3 and Low Se Content Sb2SeyS3- y Indoor Photovoltaics

Additive engineering for Sb$_2$S$_3$ indoor photovoltaics with efficiency exceeding 17%

Se-Elemental Concentration Gradient Regulation for Efficient Sb2(S,Se)3 Solar Cells With High Open-Circuit Voltages

Bandgap grading via sputtering and post-selenization using SeS2 powder enabling Sb2(S,Se)3 solar cells with 7.1% efficiency

Sputtered and Selenized Sb2Se3 Thin-Film Solar Cells with Open-Circuit Voltage Exceeding 500 Mv

An Optimization Path for Sb2(S,Se)3 Solar Cells to Achieve an Efficiency Exceeding 20

Selenium-Graded Sb-2(S1-xSex)(3) for Planar Heterojunction Solar Cell Delivering a Certified Power Conversion Efficiency of 5.71%

Vapor Transport Deposition of Sb 2 (S,Se) 3 Solar Cells with Continuously Tunable Band Gaps

Hydrothermal deposition of antimony selenosulfide thin films enables solar cells with 10% efficiency

Development of Antimony Sulfide–selenide Sb2(S, Se)3-based Solar Cells

Crystal Growth Promotion and Defects Healing Enable Minimum Open-Circuit Voltage Deficit in Antimony Selenide Solar Cells

In Situ Sulfurization to Generate Sb2(Se1 − Xsx)3 Alloyed Films and Their Application for Photovoltaics

Device engineering of Sb 2 X 3 antimony chalcogenide for loss analysis and strategies for maximizing photovoltaic efficiency

Upper efficiency limit of Sb2Se3 solar cells

Quasi-Vertically Oriented Sb 2 Se 3 Thin-Film Solar Cells with Open-Circuit Voltage Exceeding 500 mV Prepared via Close-Space Sublimation and Selenization