Abstract:Antimony chalcogenides are widely studied as a light-absorbing material due to their merits of low toxicity, efficient cost, and excellent photovoltaic properties. However, the band gaps of antimony selenide (approximately 1.1 eV) and antimony sulfide (approximately 1.7 eV) both deviate from the optimal detailed balance band gap (∼1.3 eV) for terrestrial single-junction solar cells. Notably, the band gap of Sb2(S, Se)3 can be tunable in the range from 1.1 to 1.7 eV, which can cover the detailed balance band gap. In this work, the vapor transport deposition method with two independent evaporation sources is used to deposit Sb2(S, Se)3 thin films. By carefully optimizing the evaporation temperature and the start evaporation time of the Sb2Se3 and Sb2S3 sources, a suitable band gap of 1.33 eV is obtained. Finally, on the basis of the optimal Sb2(S, Se)3 films, Sb2(S, Se)3 solar cells without a hole transport layer achieved an efficiency of 7.03%.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c10758.Saturated vapor pressure curves of Sb2Se3 and Sb2S3; temperature–time curves of Sb2Se3 and Sb2S3 sources; top-view SEM images at different Sb2Se3 and Sb2S3 source temperatures; XRD diffraction pattern under different Sb2Se3 and Sb2S3 source temperatures; transmission spectroscopy at different Sb2Se3 and Sb2S3 source temperatures; schematic diagram of thin-film light absorption; heating process of the uniform Sb2(S, Se)3 films and band gaps of Sb2(S, Se)3 films; 1/C2–V curves of the devices; band gaps of the devices obtained from EQE data; J–V curves under different light intensities; atomic and ionic radii; material parameters for SCAPS simulations; CdS trap state parameters for SCAPS simulations; and Sb2(S, Se)3 trap state parameters (PDF)This article has not yet been cited by other publications.

Bandgap grading via sputtering and post-selenization using SeS2 powder enabling Sb2(S,Se)3 solar cells with 7.1% efficiency

Se-Elemental Concentration Gradient Regulation for Efficient Sb2(S,Se)3 Solar Cells With High Open-Circuit Voltages

An Optimization Path for Sb2(S,Se)3 Solar Cells to Achieve an Efficiency Exceeding 20

HTL-Free Sb 2 (S, Se) 3 Solar Cells with an Optimal Detailed Balance Band Gap

Regulating Energy Band Alignment via Alkaline Metal Fluoride Assisted Solution Post‐Treatment Enabling Sb 2 (S,Se) 3 Solar Cells with 10.7% Efficiency

Gradient bandgap modification for highly efficient carrier transport in antimony sulfide-selenide tandem solar cells

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

Fabrication of Homogenous Sb 2 (S,Se) 3 Solar Cells by Close Space Sublimation Using a Single Alloyed Powder Source

Confined‐space selenium assisted tellurization post‐treatment strategy for efficient full‐inorganic Sb2S3 thin film solar cells

Mechanism of Defect Passivation in Sb2Se3 Solar Cells via Buried Selenium Seed Layer

Temperature‐Gradient Solution Deposition Amends Unfavorable Band Structure of Sb2(S,Se)3 Film for Highly Efficient Solar Cells

Vapor Transport Deposition of Sb 2 (S,Se) 3 Solar Cells with Continuously Tunable Band Gaps

Heterojunction Lithiation Engineering and Diffusion-Induced Defects Passivation for Highly Efficient Sb2(S,Se)3 Solar Cells

Sb2Se3 thin film solar cells in substrate configuration and the back contact selenization

Highly Efficient and Stable Planar Heterojunction Solar Cell Based on Sputtered and Post-Selenized Sb 2 Se 3 Thin Film

Preparing Cu2ZnSn(SxSe1−x)4 thin-film solar cells with front band gap grading by plasma sulfurization

Hydrazine Hydrate‐Induced Surface Modification of CdS Electron Transport Layer Enables 10.30%‐efficient Sb2(S,Se)3 Planar Solar Cells

Enhanced Photovoltaic Properties in Sb2S3 Planar Heterojunction Solar Cell with a Fast Selenylation Approach

Quasi-Vertically Oriented Sb 2 Se 3 Thin-Film Solar Cells with Open-Circuit Voltage Exceeding 500 mV Prepared via Close-Space Sublimation and Selenization

Improved Open‐Circuit Voltage of Sb 2 Se 3 Thin‐Film Solar Cells Via Interfacial Sulfur Diffusion‐Induced Gradient Bandgap Engineering

Suppressing Buried Interface Nonradiative Recombination Losses Towards High‐efficiency Antimony Triselenide Solar Cells