Abstract:The synthesis of a new resorbable porous bioactive silica-calcium phosphate composite (SCPC) that can be used as a tissue-engineering scaffold for bone regeneration is described. The effects of chemical composition and thermal treatment on crystallization and the mechanism of phase transformation in SCPC were evaluated. In the silica-rich samples, beta-rhenanite (beta-NaCaPO(4)) and alpha-cristobalite (SiO(2)) were the dominant phases after treatment at 800 degrees C. On the other hand, in the calcium phosphate-rich samples, calcium pyrophosphate (Ca(2)P(2)O(7)) was formed in addition to beta-rhenanite and alpha-cristobalaite. X-ray diffraction analyses showed a shift in the 2 theta value of the main peak(s) of all phases indicating the formation of solid solutions. Phase transformation reactions were accompanied by a loss of water molecules that contributed to the formation of pores in the size range 10-300 microm. All SCPC samples adsorbed a significantly higher quantity of serum protein than bioactive glass (p < 0.0001). In addition, the silica-rich SCPC adsorbed a significantly higher amount of serum protein than the calcium phosphate-rich samples (p < 0.003). While the crystallization of amorphous silica into L-quartz significantly inhibited serum protein adsorption, the transformation of L-quartz into alpha-cristobalite solid solution (ss) significantly enhanced protein adsorption. On the other hand, in conjunction with the transformation of brushite (CaHPO(4)) into pyro- and tri-calcium phosphates, there was a significant decrease in protein adsorption. However, as pyro- and tri-calcium phosphates transformed into beta-rhenanite, by thermal treatment, protein adsorption increased markedly. Critical-size bone defects grafted with silica-rich SCPC were filled with new bone and contained minimal residues of the graft material. Bone defects grafted with bioactive glass enhanced new bone formation, however, with very limited resorption. The enhanced resorption of SCPC in vivo correlates well with the higher rate of silica dissolution from SCPC than bioactive glass. The facilitated Si dissolution was associated with rapid bone regeneration in defects grafted with SCPC. The enhanced bioactivity properties of the SCPC are due to its chemical composition, modified crystalline structure, and high porosity. The new SCPC may be used for a wide variety of applications in the field of bone reconstruction including tissue-engineering scaffolds for cell and drug delivery.

Cuttlefish Bone-Derived Calcium Phosphate Bioceramics Have Enhanced Osteogenic Properties

Effects Bone Regeneration Using Nanotechnology – Calcium Silicate Nano-Composites.

Mechanical design of the highly porous cuttlebone: A bioceramic hard buoyancy tank for cuttlefish

Preparation and characterization of two novel osteoinductive fishbone-derived biphasic calcium phosphate bone graft substitutes

Three-Dimensional Printing of Cuttlebone-Inspired Porous Ceramic Materials

Fabrication of strontium carbonate-based composite bioceramics as potential bone regenerative biomaterials

Nano-Hydroxyapatite Derived from Biogenic and Bioinspired Calcium Carbonates: Synthesis and In Vitro Bioactivity

HA/β-TCP Biphasic Calcium Phosphate Ceramics Derived From Butterfish Bones Loaded With Bone Marrow Mesenchymal Stem Cells Promote Osteogenesis

Strontium and selenium doped bioceramics incorporated polyacrylamide-carboxymethylcellulose hydrogel scaffolds: mimicking key features of bone regeneration

Osteogenic Differentiation of Osteoblasts Induced by Calcium Silicate and Calcium Silicate/β‐tricalcium Phosphate Composite Bioceramics

Stimulatory Effects of the Ionic Products from Ca-Mg-Si Bioceramics on Both Osteogenesis and Angiogenesis in Vitro.

Transforming Natural Eggshell and Diatomite into Bioactive Calcium Silicate Material for Bone Regeneration

Fabrication of 3D printed Ca3Mg3(PO4)4-based bioceramic scaffolds with tailorable high mechanical strength and osteostimulation effect

Biomimetic Preparation of Trace Element-Codoped Calcium Phosphate for Promoting Osteoporotic Bone Defect Repair.

A novel calcium phosphate-based ceramic scaffolds with unexpected high osteogenic activity by strontium doping

3D‐Printed Bioceramic Scaffolds Reinforced by the In Situ Oriented Growth of Grains for Supercritical Bone Defect Reconstruction

Advanced bioceramic composite for bone tissue engineering: design principles and structure-bioactivity relationship

3D-printed composite, calcium silicate ceramic doped with CaSO4·2H2O: Degradation performance and biocompatibility

The Effect Of Bioactive Glass Ceramics On The Expression Of Bone-Related Genes And Proteins In Vitro

3D printing calcium phosphate ceramics with high osteoinductivity through pore architecture optimization

Fabrication of Large-Pore Mesoporous Ca-Si-based Bioceramics for Bone Regeneration.