The Study of Technology and Properties of Selective Laser Melting in Prosthodontics
Jianbo Xu,Qingmao Zhang,Liang Guo,Hongwei Wang
DOI: https://doi.org/10.14128/j.cnki.al.20173701.042
2017-01-01
Applied laser
Abstract:In order to realize the application of medical cobalt-chromium alloy in prosthodontics,using Selective Laser Melting (SLM) technology,the laser forming process was studied and developed,and the bending,tensile,hardness and heat treatment experiments were carried out.Using SEM,roughness profiler,hardness tester and other means of detection,the microstructures,mechanical properties,roughness and corrosion properties of the specimens were analyzed.Research shows the optimum parameters of SLM are as follows:laser power was 200 W,scanning speed was 500 rnm/s,slice thickness was 25 μm,scanning distance was 0.07 mm and scanning strategy was S-type X,Y,stacking fault;SLM original sample tensile strength of 1 185 MPa,hardness of 431 HV,elongation of 8.6％,fracture in the form of quasi-cleavage fracture,the tensile strength after heat treatment was 1 375 MPa,the hardness was 563 HV,the elongation was 3.1％.The corrosion potential of SLM was-717 mV,and the corrosion current density was 1.7 × 10-5 A/cm2,The corrosion potential was-10 mV and the corrosion current density was 0.3 × 10-5 A/cm2 after heat treatment.The roughness of SLM was 13.793 μm,after surface remelting,the roughness decreased to 5.141 μm,and the roughness decreased to 2.24 μm after grinding.Therefore,the heat treatment can improve the strength and corrosion resistance of the sample,but the toughness is reduced.Finally,the tooth crown bridge with high strength,low roughness and corrosion resistance was fabricated by SLM with optimized process parameters,and the wearing experiment was carried out,which accords with the performance requirements of the denture.