Anti-corrosion coatings with active and passive protective performances based on v-COF/GO nanocontainers

Meiling Zhang,Xiang Yu,Yunan Lin,Jingyuan Liu,Jun Wang

DOI: https://doi.org/10.1016/j.porgcoat.2021.106415

IF: 6.6

2021-10-01

Progress in Organic Coatings

Abstract:<p>In the present work, a novel covalent organic framework/graphene oxide nanocontainer (v-COF/GO) was synthesized via a two-step solvothermal reaction. v-COF/GO displayed a high loading capacity of benzotriazole (BTA, 17.8 wt%). The UV–Vis spectroscopy results prove that the release amount of BTA molecules can reach 90% under alkaline conditions in 15 h, which provide an effective protection for carbon steel. Electrochemical measurement results show that the impedance modulus at low frequency of v-COF//epoxy coatings was 1.3 orders of magnitude higher than that of the pure epoxy coatings even after 28 days of immersion. Moreover, the novel v-COF/GO based nanocontainer endowed the epoxy coating with efficient self-healing functionality. v-COF/ had high impermeable properties as an epoxy filler and endowed the epoxy coating with exceptional passive and active anticorrosion properties. Thus, the service life of the coating was effectively enhanced under severe conditions.</p>

materials science, coatings & films,chemistry, applied

What problem does this paper attempt to address?

### Problems Addressed by the Paper

The paper primarily addresses the issue of corrosion protection for metal materials in harsh environments. Specifically, the paper aims to achieve this goal by designing a novel covalent organic framework/graphene oxide nanocontainer (v-COF/GO). This nanocontainer can encapsulate benzotriazole (BTA) and has the following features:

1. **High Loading Capacity**: v-COF/GO has a high BTA loading capacity (approximately 17.8 wt%).
2. **Controlled Release**: Under alkaline conditions, BTA can achieve a 90% release within 15 hours, effectively protecting carbon steel.
3. **Self-Healing Function**: v-COF/GO@BTA endows the epoxy coating with an efficient self-healing function, allowing it to continue releasing BTA molecules to protect the substrate even after damage.
4. **Enhanced Anti-Corrosion Performance**: v-COF/GO@BTA, as an epoxy coating filler, significantly improves both the active and passive anti-corrosion performance of the coating.

Through these characteristics, the study aims to develop a novel anti-corrosion coating to extend the service life of coatings under harsh conditions and reduce the economic losses and resource waste caused by metal corrosion.