Corrosion-Resistant Cross-Linked Cyanate Ester Coatings Doped by Graphene Oxide for Use in High-Temperature Marine Environments

Junwei Chang,Zhenyu Wang,En-Hou Han,Qian Liu,Shuai Wang

DOI: https://doi.org/10.1021/acsanm.0c02531

IF: 6.14

2020-12-03

ACS Applied Nano Materials

Abstract:Organic coatings are widely used to protect metals from corrosion in high-temperature marine environments. Compared with inorganic or metal coatings, organic coatings exhibit favorable properties, such as a reasonable cost, adequate flexibility, and easy fabrication. However, most organic coatings are limited to relatively short protection times and thus fail to meet the increasing demands for industrial applications. In this paper, graphene oxide (GO) was added to cyanate ester (CE) coatings as a corrosion inhibitive filler. Electrochemical analysis shows that a 3 wt % GO/CE coating has favorable corrosion protection properties with a low-frequency resistance higher than 10⁶ Ω cm² and a corrosion rate of 632.9 × 10^–6 mm per year after 1320 h of immersion in a high-temperature marine environment. Top-view and cross-sectional SEM images identify the electrochemical results. Furthermore, chemical analyses by Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy demonstrate that hydroxyl groups of GO can react with cyanate groups, and therefore, a robust cross-linked structure was formed in the GO/CE coating. The synergistic effect of the physical shielding of GO and the robust cross-linked structure makes the GO/CE coating a promising choice for corrosion protection of steel in high-temperature marine environments. Our study also illustrates a novel method for preparing other chemically cross-linked composite coatings.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c02531?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c02531</a>.Potentiodynamic polarization curves of different coatings; low-frequency impedance modulus at 0.01 Hz and breakpoint frequency of all coatings; photo digital images of different CE or GO/CE-coated specimens before and after immersion in 3.5 wt % NaCl solutions; surface morphology by SEM of different coatings; contact angle of pristine CE coating, 1.5 wt % GO/CE coating, and 3 wt % GO/CE coating; bode modulus and phase angle diagrams of 0.75 wt % GO/CE coatings on Q235 steel immersed in 3.5 wt % NaCl solution from 216 to 1320 h; bode modulus and phase angle diagrams of 3 and 5 wt % GO/CE coatings on Q235 steel immersed in 3.5 wt % NaCl solution for 48, 96, 144, and 216 h, respectively; low-frequency impedance modulus at 0.01 Hz of 3 and 5 wt % GO/CE coatings with different immersion times; adhesions of six different coatings before and after immersion in 3.5 wt % NaCl solutions for 216 h; heating temperature and corresponding heating time during the whole curing process; polarization parameters of different coatings; and O₂ gas permeability of pristine CE and 3 wt % GO/CE composite membranes (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c02531/suppl_file/an0c02531_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology