Characteristics of novel Ti–10Mo-xCu alloy by powder metallurgy for potential biomedical implant applications
Wei Xu,Chenjin Hou,Yuxuan Mao,Lei Yang,Maryam Tamaddon,Jianliang Zhang,Xuanhui Qu,Chaozong Liu,Bo Su,Xin Lu
DOI: https://doi.org/10.1016/j.bioactmat.2020.04.012
IF: 18.9
2020-09-01
Bioactive Materials
Abstract:When biomaterials are implanted in the human body, the surfaces of the implants become favorable sites for microbial adhesion and biofilm formation, causing peri-implant infection which frequently results in the failure of prosthetics and revision surgery. Ti-Mo alloy is one of the commonly used implant materials for load-bearing bone replacement, and the prevention of infection of Ti-Mo implants is therefore crucial. In this study, bacterial inhibitory copper (Cu) was added to Ti-Mo matrix to develop a novel Ti-Mo-Cu alloy with bacterial inhibitory property. The effects of Cu content on microstructure, tensile properties, cytocompatibility, and bacterial inhibitory ability of Ti-Mo-Cu alloy were systematically investigated. Results revealed that Ti-10Mo-1Cu alloy consisted of α and β phases, while there were a few Ti<sub>2</sub>Cu intermetallic compounds existed for Ti-10Mo-3Cu and Ti-10Mo-5Cu alloys, in addition to α and β phases. The tensile strength of Ti-10Mo-xCu alloy increased with Cu content while elongation decreased. Ti-10Mo-3Cu alloy exhibited an optimal tensile strength of 1098.1 MPa and elongation of 5.2%. Cytocompatibility study indicated that none of the Ti-10Mo-xCu alloys had a negative effect on MC3T3-E1 cell proliferation. Bacterial inhibitory rates against <i>S. aureus</i> and <i>E. coli</i> increased with the increase in Cu content of Ti-10Mo-xCu alloy, within the ranges of 20-60% and 15-50%, respectively. Taken together, this study suggests that Ti-10Mo-3Cu alloy with high strength, acceptable elongation, excellent cytocompatibility, and the bacterial inhibitory property is a promising candidate for biomedical implant applications.
engineering, biomedical,materials science, biomaterials